Solvay Specialty Polymers Torlon® 4301 Polyamide-imide (PAI)

Category Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Extruded
Manufacturer Solvay Specialty Polymers
Trade Name Torlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Torlon® 4301 Polyamide-imide (PAI).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Torlon® 4301 is a wear-resistant grade of polyamide-imide (PAI) resin. It has a good balance of mechanical properties and wear resistance. It offers high flexural and compressive strength with a low coefficient of friction and outstanding wear resistance at both high velocity and high pressure conditions.Features: Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Wear Resistance; High Heat Resistance; High Temperature Strength; Low Friction; Self Lubricating; Semi ConductiveUses: Aerospace Applications; Aircraft Applications; Automotive Applications; Bearings; Bushings; Cams; Gears; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Oil/Gas Applications; Rollers; Sealing Devices; Seals; Thrust Washer; Transmission Applications; WasherAdditional Properties: Coefficient of Linear Thermal Expansion - ASTM D696 2.5E-5 cm/cm/°C; Wear Factor - ASTM D3702 14.0 in³·min^-10/ft·lb·hr; Wear Factor - ASTM D3702 17.0 in³·min^-10/ft·lb·hr; Wear Factor - ASTM D3702 9.00 in³·min^-10/ft·lb·hr; Wear Factor - ASTM D3702 0.400 in³·min^-10/ft·lb·hrAutomotive Specifications BOSCH N28 BN05-OX2 N28 BN05-OX2, BN0512-CDSX-0Cgr01SOInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Water Absorption 0.28 %

@Time 86400 sec
0.28 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength 113 MPa
16400 psi
ASTM D638
Tensile Stress 163 MPa
23600 psi
ASTM D1708
Tensile Modulus 6.55 GPa
950 ksi
ASTM D638
Flexural Strength 112 MPa

@Temperature 232 °C
16200 psi

@Temperature 450 °F
ASTM D790
215 MPa

@Temperature 23.0 °C
31200 psi

@Temperature 73.4 °F
ASTM D790
Flexural Modulus 4.96 GPa

@Temperature 232 °C
719 ksi

@Temperature 450 °F
ASTM D790
6.89 GPa

@Temperature 23.0 °C
999 ksi

@Temperature 73.4 °F
ASTM D790
Compressive Strength 166 MPa
24100 psi
ASTM D695
Compressive Modulus 5.31 GPa
770 ksi
ASTM D695
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.10 J/cm
7.68 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.530 W/m-K
3.68 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 279 °C
534 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 8.00e+15 ohm-cm
8.00e+15 ohm-cm
ASTM D257
Surface Resistance 8.00e+17 ohm
8.00e+17 ohm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 304 °C
579 °F
Nozzle Temperature 371 °C
700 °F
Mold Temperature 199 - 216 °C
390 - 421 °F
Drying Temperature 177 °C

@Time 10800 sec
351 °F

@Time 3.00 hour
Moisture Content <= 0.050 %
<= 0.050 %
Back Pressure 6.89 MPa
999 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Additive PTFE + Graphite Lubricant
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Form Pellets
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw L/D Ratio 18.0:1.0 to 24.0:1.0