- Solvay Specialty Polymers Ryton® XE5515BL Polyphenylene Sulfide Alloy (PPS Alloy), 15% Glass Fiber
Solvay Specialty Polymers Ryton® XE5515BL Polyphenylene Sulfide Alloy (PPS Alloy), 15% Glass Fiber
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ryton® XE5515BL Polyphenylene Sulfide Alloy (PPS Alloy), 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ryton® XE5515BL 15% glass fiber reinforced polyphenylene sulfide alloy compound provides excellent mechanical strength and chemical resistance at elevated temperatures and is suitable for extrusion or blow molding.Features: Good Chemical Resistance; Good StrengthInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Filler Content | 15 % | 15 % | Glass Fiber |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.18 mm |
0.0050 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 316 °C |
12 g/10 min @Load 11.0 lb, Temperature 601 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 118 | 118 | ASTM D785 |
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength | 103 MPa | 14900 psi | ASTM D638 |
| Tensile Stress | 110 MPa | 16000 psi | ISO 527-2 |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-2 |
| 2.9 % | 2.9 % | ASTM D638 | |
| Tensile Modulus | 5.80 GPa | 841 ksi | ISO 527-2 |
| 6.21 GPa | 901 ksi | ASTM D638 | |
| Flexural Strength | 159 MPa | 23100 psi | ASTM D790 |
| 170 MPa | 24700 psi | ISO 178 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 |
| 5.52 GPa | 801 ksi | ASTM D790 | |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Izod Impact, Notched | 0.960 J/cm @Thickness 3.18 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 6.90 J/cm @Thickness 3.18 mm |
12.9 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 100 - 200 °C |
11.1 µin/in-°F @Temperature 212 - 392 °F |
2 |
| 30.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
16.7 µin/in-°F @Temperature -58.0 - 122 °F |
2 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
30.6 µin/in-°F @Temperature -58.0 - 122 °F |
TMA; ASTM E831 |
| 90.0 µm/m-°C @Temperature 100 - 200 °C |
50.0 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 50 % | 50 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Insulation Resistance | 1.00e+13 ohm @Temperature 90.0 °C |
1.00e+13 ohm @Temperature 194 °F |
IEC 60167 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.6 @Frequency 1000 Hz |
3.6 @Frequency 1000 Hz |
ASTM D150 | |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz |
0.0020 @Frequency 1000 Hz |
ASTM D150 |
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 100 sec | 100 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | UL 746 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Processing Technique | Blow Molding; Extrusion | |
| RoHS Compliance | RoHS Compliant |