Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide (PPS), 40% Glass Fiber

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Solvay Specialty Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide (PPS), 40% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ryton® R-4-230NA and R-4-230BL 40% glass fiber reinforced polyphenylene sulfide compounds provide reduced flash and improved processability compared to other polyphenylene sulfide injection molding compounds.Features: Good ProcessabilityInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ASTM D792
Filler Content 40 %
40 %
Glass Fiber
Water Absorption 0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 3.18 mm
0.0020 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm

@Thickness 3.20 mm
0.0050 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 104
104
ASTM D785
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength 165 MPa
23900 psi
ASTM D638
Tensile Stress 145 MPa
21000 psi
ISO 527-2
Elongation at Break 1.1 %
1.1 %
ISO 527-2
1.2 %
1.2 %
ASTM D638
Flexural Strength 210 MPa
30500 psi
ISO 178
221 MPa
32100 psi
ASTM D790
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
14.5 GPa
2100 ksi
ASTM D790
Compressive Strength 275 MPa
39900 psi
ASTM D695
Poissons Ratio 0.43
0.43
ASTM E132
Izod Impact, Notched 0.800 J/cm

@Thickness 3.18 mm
1.50 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.00 J/cm

@Thickness 3.18 mm
7.49 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
Notch A; ISO 180
Izod Impact, Unnotched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature 100 - 200 °C
8.33 µin/in-°F

@Temperature 212 - 392 °F
2
15.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
8.33 µin/in-°F

@Temperature -58.0 - 122 °F
2
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
22.2 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
80.0 µm/m-°C

@Temperature 100 - 200 °C
44.4 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
ASTM C177
Maximum Service Temperature, Air 200 - 220 °C
392 - 428 °F
UL Temperature Rating
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
Oxygen Index 50 %
50 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Insulation Resistance 1.00e+12 ohm

@Temperature 90.0 °C
1.00e+12 ohm

@Temperature 194 °F
IEC 60167
Dielectric Constant 3.9

@Frequency 1000 Hz
3.9

@Frequency 1000 Hz
ASTM D150
3.9

@Frequency 1.00e+6 Hz
3.9

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
ASTM D150
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 125 sec
125 sec
ASTM D495
Comparative Tracking Index 150 V
150 V
UL 746
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant