Solvay Specialty Polymers Primef® 4002 40% GF PPS, High Fluidity Grade  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Primef® 4002 40% GF PPS, High Fluidity Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Used for injection molding of high performance parts.
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Solvay Test Method
Spiral Flow 25.0 cm

@Temperature 300 °C
9.84 in

@Temperature 572 °F
Solvay Method
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 160 MPa
23200 psi
ISO 527
Elongation at Break 1.6 %
1.6 %
ISO 527
Tensile Modulus 13.0 GPa
1890 ksi
ISO 527
Flexural Strength 225 MPa
32600 psi
ISO 178
Flexural Modulus 13.0 GPa
1890 ksi
ISO 178
Izod Impact, Notched 0.650 J/cm
1.22 ft-lb/in
ISO 180
Izod Impact, Unnotched 2.50 J/cm
4.68 ft-lb/in
ISO 180
Thermal Properties Metric English Comments
Thermal Conductivity 0.500 W/m-K
3.47 BTU-in/hr-ft²-°F
ISO 8302
Melting Point 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
ISO 75
Glass Transition Temp, Tg 90.0 °C
194 °F
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Oxygen Index 52 %
52 %
ISO 4589
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 93/167
Dielectric Constant 3.9

@Frequency 1.00e+6 Hz
3.9

@Frequency 1.00e+6 Hz
IEC 250
4.0

@Frequency 1000 Hz
4.0

@Frequency 1000 Hz
IEC 250
Dielectric Strength 17.0 kV/mm
432 kV/in
IEC 243
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
IEC 250
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
IEC 250
Comparative Tracking Index 150 V
150 V
IEC 112
Processing Properties Metric English Comments
Nozzle Temperature 320 - 350 °C
608 - 662 °F
Melt Temperature 320 - 330 °C
608 - 626 °F
Mold Temperature 150 - 160 °C
302 - 320 °F