Solvay Specialty Polymers Polidan® PNT 0553/23 Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable
Manufacturer Solvay Specialty Polymers
Trade Name Polidan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Polidan® PNT 0553/23 Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
POLIDAN® PNT 0553/23 is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction.Features: Crosslinkable; Good Flexibility; Low DensityUses: Connectors; Hose; Rubber ReplacementAdditional Properties: Extruder Screw Compression Ratio - >2.5:1; Extruder Screw L/D Ratio - 25:1 to 30:1; Gel Content - EN 579 > 65 %; Head Temperature - 200 °CInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 0.902 g/cc
0.0326 lb/in³
ASTM D792
Melt Flow 0.40 g/10 min
0.40 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength >= 20.0 MPa
>= 2900 psi
ASTM D638
Elongation at Break >= 400 %
>= 400 %
ASTM D638
Tensile Modulus 0.0280 GPa
4.06 ksi
ISO 527-2
Thermal Properties Metric English Comments
Specific Heat Capacity 2.03 J/g-°C
0.485 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.450 - 0.470 W/m-K
3.12 - 3.26 BTU-in/hr-ft²-°F
ASTM C177
Vicat Softening Point 84.0 °C
183 °F
ASTM D1525
Processing Properties Metric English Comments
Zone 1 150 - 200 °C
302 - 392 °F
Zone 2 150 - 200 °C
302 - 392 °F
Zone 3 150 - 200 °C
302 - 392 °F
Zone 4 150 - 200 °C
302 - 392 °F
Zone 5 150 - 200 °C
302 - 392 °F
Die Cooling Temperature 210 °C
410 °F
Descriptive Properties Value Comments
Agency Ratings DVGW W270; KTW Unspecified Rating
Availability Asia Pacific
Europe
North America
Processing Technique Extrusion; Pipe Extrusion