- Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK), 30% Carbon Fiber
Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK), 30% Carbon Fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | KetaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK), 30% Carbon Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KetaSpire® KT-880 CF30 is a high flow, 30% carbon fiber reinforced grade of polyetheretherketone (PEEK). Carbon-fiber reinforcement of KetaSpire® PEEK provides the maximum levels of mechanical properties at temperatures approaching 300°C and the lowest coefficient of linear thermal expansion within the KetaSpire® product family.Features: Autoclave Sterilizable; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Sterilizability; Heat Sterilizable; High Flow; High Heat Resistance; High Stiffness; High Strength; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam SterilizableUses: Aircraft Applications; Connectors; Dental Applications; Electrical/Electronic Applications; Film; Hospital Goods; Industrial Applications; Medical Devices; Medical/Healthcare Applications; Oil/Gas Applications; Pump Parts; Seals; Surgical InstrumentsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Carbon Fiber |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 450000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
450000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm @Thickness 3.18 mm |
0.00 - 0.0020 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Thickness 3.18 mm |
0.014 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 400 °C |
11 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 106 | 106 | ASTM D785 |
| Tensile Strength | 223 MPa | 32300 psi | ASTM D638 |
| Tensile Strength, Yield | 218 MPa | 31600 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 1.7 % | 1.7 % | Type 1A, 5 mm/min; ISO 527-2 |
| 1.7 % | 1.7 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 20.9 GPa | 3030 ksi | ASTM D638 |
| 25.4 GPa | 3680 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 319 MPa | 46300 psi | ISO 178 |
| 321 MPa | 46600 psi | ASTM D790 | |
| Flexural Modulus | 17.9 GPa | 2600 ksi | ASTM D790 |
| 21.5 GPa | 3120 ksi | ISO 178 | |
| Compressive Strength | 188 MPa | 27300 psi | ASTM D695 |
| Shear Strength | 103 MPa | 14900 psi | ASTM D732 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.70 µm/m-°C @Temperature -50.0 - 50.0 °C |
3.72 µin/in-°F @Temperature -58.0 - 122 °F |
1 |
| Specific Heat Capacity | 1.31 J/g-°C @Temperature 50.0 °C |
0.313 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.81 J/g-°C @Temperature 200 °C |
0.433 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 343 °C | 649 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 147 °C | 297 °F | DSC |
| Flammability, UL94 | V-0 @Thickness 0.800 - 1.60 mm |
V-0 @Thickness 0.0315 - 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 365 °C | 689 °F | |
| Middle Barrel Temperature | 370 °C | 698 °F | |
| Front Barrel Temperature | 375 °C | 707 °F | |
| Nozzle Temperature | 380 °C | 716 °F | |
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |
| Drying Temperature | 150 °C @Time 14400 sec |
302 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | FAA FAR 25.853a | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hybrid S493 ABS + Polycarbonate Alloy
- Shandong Rike Chemical RIKEâ„¢ RK-760G MBS Impact Modifier for PVC Transparent Product
- SABIC Innovative Plastics Xenoy® CL402U PBT+PC (Europe-Africa-Middle East)
- SSAB Tunnplat Aluzink 260A RP-X High-strength Metal-coated Steel
- Chesterton ARC S7 High Temperature & Chemical Resistant Novolac Vinyl Ester Coating
- DuPont Performance Polymers Crastin® HR5330HF BK503 Polybutylene Terephthalate (PBT) (Unverified Data**)&
- BASF Ultramid® B3WG6 CR BK 23210 15% Glass Filled (Dry)
- A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy
- Fainplast Compounds PM 6640 Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved