- Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, DAM (discontinued **)
Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, DAM (discontinued **)
| Category | Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, DAM
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay Advanced Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | Carbon |
| Water Absorption | 0.22 % | 0.22 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 65% RH; Solvay Test |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm | 0.00050 - 0.0015 in/in | Solvay Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 250 MPa | 36300 psi | ISO 527 |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| Tensile Modulus | 26.0 GPa | 3770 ksi | ISO 527 |
| Flexural Strength | 340 MPa | 49300 psi | ISO 178 |
| Flexural Modulus | 24.0 GPa | 3480 ksi | ISO 178 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ISO 180 |
| Izod Impact, Unnotched | 4.50 J/cm | 8.43 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.750 W/m-K | 5.20 BTU-in/hr-ft²-°F | ISO 8302 |
| Melting Point | 240 °C | 464 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3000 ohm-cm | 3000 ohm-cm | ISO 3915 |
| Surface Resistance | 200 ohm | 200 ohm | ISO 3915 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 280 °C | 482 - 536 °F | |
| Rear Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Compression Zone |
| Middle Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Homogenization Zone |
| Front Barrel Temperature | 260 - 290 °C | 500 - 554 °F | Nozzle Zone |
| Melt Temperature | 280 °C | 536 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | Needed to develop high crystallinity |
| Injection Pressure | 50.0 - 250 MPa | 7250 - 36300 psi | |
| Hold Pressure | 30.0 - 150 MPa | 4350 - 21800 psi | |
| Back Pressure | 0.000 - 1.00 MPa | 0.000 - 145 psi |