Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, at Equilibrium (65% RH)  

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, at Equilibrium (65% RH)  .pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay Advanced Polymers.
Physical Properties Metric English Comments
Density 1.85 g/cc
0.0668 lb/in³
Dry as molded
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 120 MPa
17400 psi
ASTM D638
Elongation at Break 1.3 %
1.3 %
ASTM D638
Tensile Modulus 18.0 GPa
2610 ksi
ASTM D638
Flexural Yield Strength 175 MPa
25400 psi
ASTM D790
Flexural Modulus 16.5 GPa
2390 ksi
ASTM D790
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.80 J/cm
5.25 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 240 °C
464 °F
Processing Properties Metric English Comments
Feed Temperature 250 - 280 °C
482 - 536 °F
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Compression Zone
Middle Barrel Temperature 250 - 280 °C
482 - 536 °F
Homogenization Zone
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Zone
Melt Temperature <= 270 °C
<= 518 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Needed to develop high crystallinity
Injection Pressure 50.0 - 250 MPa
7250 - 36300 psi
Hold Pressure 30.0 - 150 MPa
4350 - 21800 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi