Solvay Specialty Polymers Ixef® 2030 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 2030 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 2030 is a 55% glass-fiber/mineral reinforced polyarylamide compound which exhibits high strength, very high stiffness, low warpage, excellent creep resistance and outstanding surface gloss. - Black Ixef 2030/X927 - Custom ColorableInjection Notes: Hot Runners: 250°C to 260°C (482°F to 500°F) Injection pressure: rapid Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 2030 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 290°C (500°F to 554°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.74 g/cc
0.0629 lb/in³
ISO 1183
Filler Content 55 %
55 %
GlassMineral
Water Absorption 0.19 %

@Temperature 23.0 °C,
Time 86400 sec
0.19 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
65% RH; Internal Method
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
Internal Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ISO 527-2
Elongation at Break 1.2 %
1.2 %
ISO 527-2
Tensile Modulus 21.5 GPa
3120 ksi
ISO 527-2
Flexural Strength 220 MPa
31900 psi
ISO 178
Flexural Modulus 19.0 GPa
2760 ksi
ISO 178
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
2.70 J/cm
5.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C
10.0 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB
HB
UL 94
Oxygen Index 26 %
26 %
ISO 4589-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.8

@Frequency 110 Hz
4.8

@Frequency 110 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.025

@Frequency 110 Hz
0.025

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Appearance Black
Colors Available
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Strength
High Flow
High Stiffness
Low Moisture Absorption
Low Warpage
Outstanding Surface Finish
Forms Pellets
Generic PARA
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Electronics
Business Equipment
Cams
Furniture
Gears
Industrial Applications
Lawn and Garden Equipment
Machine/Mechanical Parts
Metal Replacement
Power/Other Tools