Solvay Specialty Polymers Ixef® 2030 Polyarylamide (PARA), 55% GlassMineral

Category Polymer , Thermoplastic , Polyarylamide (PAA)
Manufacturer Solvay Specialty Polymers
Trade Name Ixef®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 2030 Polyarylamide (PARA), 55% GlassMineral.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef® 2030 is a 55% glass-fiber/mineral reinforced polyarylamide compound which exhibits high strength, very high stiffness, low warpage, excellent creep resistance and outstanding surface gloss.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Strength; High Flow; High Stiffness; Low Moisture Absorption; Low Warpage; Outstanding Surface FinishUses: Automotive Applications; Automotive Electronics; Business Equipment; Cams; Furniture; Gears; Industrial Applications; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Additional Properties: Moisture Absorption - Internal Method 1.6 %Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.74 g/cc
0.0629 lb/in³
ISO 1183
Filler Content 55 %
55 %
GlassMineral
Water Absorption 0.19 %

@Time 86400 sec
0.19 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ISO 527-2
Elongation at Break 1.2 %
1.2 %
ISO 527-2
Tensile Modulus 21.5 GPa
3120 ksi
ISO 527-2
Flexural Strength 220 MPa
31900 psi
ISO 178
Flexural Modulus 19.0 GPa
2760 ksi
ISO 178
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.70 J/cm
5.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C
10.0 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB
HB
Oxygen Index 26 %
26 %
ISO 4589-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IIEC 60093
Dielectric Constant 4.8

@Frequency 1.10e+8 Hz
4.8

@Frequency 1.10e+8 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.025

@Frequency 110 Hz
0.025

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C

@Time 1800 - 5400 sec
248 °F

@Time 0.500 - 1.50 hour
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Colors
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant