Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, DAM  (discontinued **)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, DAM  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay Advanced Polymers.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ASTM D792
Water Absorption 0.18 %
0.18 %
24 hrs; ASTM D570
Moisture Absorption at Equilibrium 1.8 %
1.8 %
at 65% RH per Solvay test
Linear Mold Shrinkage, Flow 0.0055 cm/cm
0.0055 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 105 MPa
15200 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ASTM D638
Tensile Modulus 9.50 GPa
1380 ksi
ASTM D638
Flexural Yield Strength 180 MPa
26100 psi
ASTM D790
Flexural Modulus 8.50 GPa
1230 ksi
ASTM D790
Izod Impact, Notched 0.400 J/cm
0.749 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.30 J/cm
6.18 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 32.0 µm/m-°C

@Temperature 20.0 °C
17.8 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Thermal Conductivity 0.500 W/m-K
3.47 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
HDT/A; ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB UL Rating ; Solvay test
Electrical Properties Metric English Comments
Electrical Resistivity 4.00e+15 ohm-cm
4.00e+15 ohm-cm
ASTM D257
Dielectric Constant 4.4

@Frequency 110 Hz
4.4

@Frequency 110 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm
584 kV/in
ASTM D149
Dissipation Factor 0.017

@Frequency 110 Hz
0.017

@Frequency 110 Hz
ASTM D150
Arc Resistance >= 60 sec
>= 60 sec
ASTM D495
Comparative Tracking Index 550 V
550 V
IEC 112
Processing Properties Metric English Comments
Feed Temperature 250 - 280 °C
482 - 536 °F
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Compression Zone
Middle Barrel Temperature 250 - 280 °C
482 - 536 °F
Homogenization Zone
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Zone
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Needed to develop high crystallinity
Injection Pressure 50.0 - 250 MPa
7250 - 36300 psi
Hold Pressure 30.0 - 150 MPa
4350 - 21800 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi