Solvay Specialty Polymers Ixef® 1313/0004 Polyarylamide, 40% Glass Fiber + Elastomer, at Equilibrium (65% RH)  

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1313/0004 Polyarylamide, 40% Glass Fiber + Elastomer, at Equilibrium (65% RH)  .pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modified. The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay Advanced Polymers.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
DAM; ISO 1183
Filler Content 40 %
40 %
Glass
Water Absorption 0.21 %
0.21 %
24 hr (DAM); ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
65% RH (beginning DAM); Solvay Test
Linear Mold Shrinkage, Flow 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
Solvay Test
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
Tensile Modulus 9.50 GPa
1380 ksi
ISO 527
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ISO 180
Izod Impact, Unnotched 7.50 J/cm
14.1 ft-lb/in
ISO 180
Thermal Properties Metric English Comments
Melting Point 240 °C
464 °F
Processing Properties Metric English Comments
Feed Temperature 250 - 280 °C
482 - 536 °F
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Compression Zone
Middle Barrel Temperature 250 - 280 °C
482 - 536 °F
Homogenization Zone
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Zone
Melt Temperature <= 270 °C
<= 518 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Needed to develop high crystallinity
Injection Pressure 50.0 - 250 MPa
7250 - 36300 psi
Hold Pressure 30.0 - 150 MPa
4350 - 21800 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi