Solvay Specialty Polymers Halar® 300 ECTFE Fluoropolymer  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , ECTFE Fluoropolymer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Halar® 300 ECTFE Fluoropolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer.HALAR® Fluoropolymers have excellent barrier properties, high resistance to a variety of corrosive chemicals and solvents, low flammability, and ease of processing.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
Water Absorption <= 0.10 %
<= 0.10 %
168 hours
Moisture Absorption at Equilibrium <= 0.10 %
<= 0.10 %
after 168 hours
Mechanical Properties Metric English Comments
Hardness, Rockwell R 90
90
Hardness, Shore D 75
75
Tensile Strength, Ultimate 54.0 MPa
7830 psi
Tensile Strength, Yield 30.0 MPa
4350 psi
Elongation at Break 250 %
250 %
Elongation at Yield 5.0 %
5.0 %
Tensile Modulus 1.655 GPa
240.0 ksi
Flexural Yield Strength 47.0 MPa
6820 psi
Flexural Modulus 1.69 GPa
245 ksi
Izod Impact, Notched 1.22 J/cm

@Temperature -40.0 °C
2.29 ft-lb/in

@Temperature -40.0 °F
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Tensile Impact Strength 806 kJ/m²
384 ft-lb/in²
ASTM D1822S
Coefficient of Friction, Dynamic 0.19
0.19
vs. steel; 50 cm/s (20 in/s); ASTM D1044
Coefficient of Friction, Static 0.19
0.19
vs. steel; ASTM D1044
Taber Abrasion, mg/1000 Cycles 5.0
5.0
CS-17 wheels; 500 g; wheels cleaned every 25 cycles
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature -30.0 - 50.0 °C
44.4 µin/in-°F

@Temperature -22.0 - 122 °F
135 µm/m-°C

@Temperature 85.0 - 125 °C
75.0 µin/in-°F

@Temperature 185 - 257 °F
Specific Heat Capacity 0.946 J/g-°C
0.226 BTU/lb-°F
Thermal Conductivity 0.151 W/m-K
1.05 BTU-in/hr-ft²-°F
Melting Point 240 °C
464 °F
Maximum Service Temperature, Air 150 °C
302 °F
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
Brittleness Temperature <= -76.0 °C
<= -105 °F
Flammability, UL94 V-0

@Thickness 0.180 mm
V-0

@Thickness 0.00709 in
Oxygen Index >= 52 %
>= 52 %
Optical Properties Metric English Comments
Refractive Index 1.4476

@Wavelength 589 nm
1.4476

@Wavelength 589 nm
Halar® 500
Haze 3.0 - 5.0 %
3.0 - 5.0 %
typical for HALAR films; ASTM D1003
Gloss 85 - 95 %
85 - 95 %
85-95% at 20° is typical of HALAR films; ASTM D2457
Electrical Properties Metric English Comments
Electrical Resistivity 1.56e+16 ohm-cm
1.56e+16 ohm-cm
Surface Resistance >= 1.00e+17 ohm
>= 1.00e+17 ohm
ASTM D257
Dielectric Constant 2.5

@Frequency 1000 Hz
2.5

@Frequency 1000 Hz
2.59

@Frequency 1e+6 Hz
2.59

@Frequency 1e+6 Hz
Dielectric Strength 14.0 kV/mm

@Thickness 3.18 mm
356 kV/in

@Thickness 0.125 in
21.0 kV/mm

@Thickness 1.60 mm
533 kV/in

@Thickness 0.0630 in
80.0 kV/mm

@Thickness 0.0250 mm
2030 kV/in

@Thickness 0.000984 in
Dissipation Factor 0.0016

@Frequency 1000 Hz
0.0016

@Frequency 1000 Hz
0.014

@Frequency 1e+6 Hz
0.014

@Frequency 1e+6 Hz
Arc Resistance >= 50 sec
>= 50 sec
Test Terminated at 50 sec.; ASTM D495
Comparative Tracking Index >= 600 V

@Thickness 1.60 mm
>= 600 V

@Thickness 0.0630 in
Hot Wire Ignition, HWI 20.2 sec

@Thickness 1.60 mm
20.2 sec

@Thickness 0.0630 in
High Amp Arc Ignition, HAI >= 200 arcs

@Thickness 1.60 mm
>= 200 arcs

@Thickness 0.0630 in
test terminated at 200 arcs 1/16 A.S.
High Voltage Arc-Tracking Rate, HVTR 208 mm/min

@Thickness 1.60 mm
8.19 in/min

@Thickness 0.0630 in
Processing Properties Metric English Comments
Processing Temperature 260 - 282 °C
500 - 540 °F