Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stability, lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. - Natural: AvaSpire AV-848 NTInjection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
ASTM D570
Viscosity 500000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
500000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt; ASTM D3835
Mechanical Properties Metric English Comments
Tensile Strength 94.0 MPa
13600 psi
50 mm/min; ASTM D638
Elongation at Break 35 %
35 %
50 mm/min; ASTM D638
75 %
75 %
5.1 mm/min; ASTM D638
Elongation at Yield 6.7 %
6.7 %
50 mm/min; ASTM D638
Tensile Modulus 3.10 GPa
450 ksi
50 mm/min; ASTM D638
Flexural Strength 134 MPa
19400 psi
ASTM D790
Flexural Modulus 3.30 GPa
479 ksi
ASTM D790
Compressive Strength 118 MPa
17100 psi
ASTM D695
Shear Strength 82.0 MPa
11900 psi
ASTM D732
Izod Impact, Notched 0.750 J/cm
1.41 ft-lb/in
ASTM D256
NB
NB
ASTM D4812
Thermal Properties Metric English Comments
Specific Heat Capacity 1.65 J/g-°C

@Temperature 50.0 °C
0.394 BTU/lb-°F

@Temperature 122 °F
DSC
1.66 J/g-°C

@Temperature 200 °C
0.397 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 340 °C
644 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 252 °C
486 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
ASTM D3418
Electrical Properties Metric English Comments
Dielectric Constant 3.18

@Frequency 1.00e+6 Hz
3.18

@Frequency 1.00e+6 Hz
ASTM D150
3.21

@Frequency 60.0 Hz
3.21

@Frequency 60.0 Hz
ASTM D150
3.23

@Frequency 1000 Hz
3.23

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 180 kV/mm

@Thickness 0.0500 mm
4570 kV/in

@Thickness 0.00197 in
Amorphous Film; ASTM D149
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
ASTM D150
0.0020

@Frequency 60.0 Hz
0.0020

@Frequency 60.0 Hz
ASTM D150
0.0060

@Frequency 1.00e+6 Hz
0.0060

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 382 - 404 °C
720 - 759 °F
Mold Temperature 166 - 193 °C
331 - 379 °F
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Natural Color
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Ductile
Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Impact Resistance
High Heat Resistance
Forms Pellets
Generic PAEK
Injection Rate Fast
Processing Method Extrusion Blow Molding
Fiber (Spinning) Extrusion
Film Extrusion
Injection Blow Molding
Injection Molding
Machining
Profile Extrusion
Thermoforming
Wire & Cable Extrusion
Screw Compression Ratio 2.0:1.0 to 3.0:1.0
Uses Oil/Gas Applications
Seals
Users viewing this material also viewed the following: