Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AvaSpire AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of reinforced PEEK. These include: improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 GF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire PAEK can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion. - Natural: AvaSpire AV-848 NTInjection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Specific Gravity	1.53 g/cc	1.53 g/cc	ASTM D792
Filler Content	30 %	30 %	Glass Fiber Reinforcement
Water Absorption	0.10 % @Time 86400 sec	0.10 % @Time 24.0 hour	ASTM D570
Viscosity	60000 cP @Shear Rate 1000 1/s, Temperature 400 °C	60000 cP @Shear Rate 1000 1/s, Temperature 752 °F	Melt; ASTM D3835
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm @Thickness 3.18 mm	0.0020 - 0.0040 in/in @Thickness 0.125 in	5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Thickness 3.18 mm	0.0050 - 0.0070 in/in @Thickness 0.125 in	5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 400 °C	9.0 g/10 min @Load 4.76 lb, Temperature 752 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength	168 MPa	24400 psi	5.0 mm/min; ASTM D638
Elongation at Break	2.3 %	2.3 %	5.0 mm/min; ASTM D638
Tensile Modulus	10.6 GPa	1540 ksi	5.0 mm/min; ASTM D638
Flexural Strength	239 MPa	34700 psi	ASTM D790
Flexural Modulus	9.90 GPa	1440 ksi	ASTM D790
Compressive Strength	139 MPa	20200 psi	ASTM D695
Shear Strength	84.8 MPa	12300 psi	ASTM D732
Izod Impact, Notched	0.690 J/cm	1.29 ft-lb/in	ASTM D256
	9.60 J/cm	18.0 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.30 J/g-°C @Temperature 50.0 °C	0.311 BTU/lb-°F @Temperature 122 °F	DSC
	1.70 J/g-°C @Temperature 200 °C	0.406 BTU/lb-°F @Temperature 392 °F	DSC
Thermal Conductivity	0.290 W/m-K	2.01 BTU-in/hr-ft²-°F	ASTM E1530
Melting Point	340 °C	644 °F	Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	257 °C @Thickness 3.20 mm	495 °F @Thickness 0.126 in	Annealed; 2 hours at 200°C; ASTM D648
Glass Transition Temp, Tg	158 °C	316 °F	DSC

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.80e+17 ohm-cm	1.80e+17 ohm-cm	ASTM D257
Surface Resistance	>= 1.90e+17 ohm	>= 1.90e+17 ohm	ASTM D257
Dielectric Constant	3.69 @Frequency 1.00e+6 Hz	3.69 @Frequency 1.00e+6 Hz	ASTM D150
	3.74 @Frequency 60.0 Hz	3.74 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	18.0 kV/mm @Thickness 3.00 mm	457 kV/in @Thickness 0.118 in	ASTM D149
Dissipation Factor	0.0020 @Frequency 60.0 Hz	0.0020 @Frequency 60.0 Hz	ASTM D150
	0.0060 @Frequency 1.00e+6 Hz	0.0060 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English
Rear Barrel Temperature	366 °C	691 °F
Middle Barrel Temperature	371 °C	700 °F
Front Barrel Temperature	377 °C	711 °F
Nozzle Temperature	382 °C	720 °F
Melt Temperature	382 - 404 °C	720 - 759 °F
Mold Temperature	166 - 193 °C	331 - 379 °F
Drying Temperature	149 °C	300 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Appearance	Natural Color
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Fatigue Resistant
	Flame Retardant
	Good Chemical Resistance
	Good Dimensional Stability
	High Heat Resistance
	High Stiffness
	High Strength
Forms	Pellets
Generic	PAEK
Injection Rate	Fast
Processing Method	Injection Molding
	Machining
	Profile Extrusion
Screw Compression Ratio	2.0:1.0 to 3.0:1.0
Uses	Oil/Gas Applications
	Seals