Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-848 CF30 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire AV-848 CF30 is a 30% carbon fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of PEEK. These include: improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 CF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire AV-848 CF30 can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion.Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Filler Content 30 %
30 %
Carbon Fiber Reinforcement
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.00 - 0.0020 cm/cm
0.00 - 0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 400 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 176 MPa
25500 psi
5.0 mm/min; ASTM D638
Elongation at Break 1.5 %
1.5 %
5.0 mm/min; ASTM D638
Tensile Modulus 18.8 GPa
2730 ksi
5.0 mm/min; ASTM D638
Flexural Strength 259 MPa
37600 psi
ASTM D790
Flexural Modulus 16.5 GPa
2390 ksi
ASTM D790
Compressive Strength 145 MPa
21000 psi
ASTM D695
Shear Strength 95.0 MPa
13800 psi
ASTM D732
Izod Impact, Notched 0.430 J/cm
0.806 ft-lb/in
ASTM D256
5.30 J/cm
9.93 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.0370 W/m-K
0.257 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 340 °C
644 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 257 °C
495 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
DSC
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 382 - 404 °C
720 - 759 °F
Mold Temperature 166 - 193 °C
331 - 379 °F
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
High Heat Resistance
High Stiffness
High Strength
Forms Pellets
Generic PAEK
Injection Rate Fast
Processing Method Injection Molding
Machining
Profile Extrusion
Screw Compression Ratio 2.0:1.0 to 3.0:1.0
Uses Bearings
Bushings
Oil/Gas Applications
Seals
Wear Strip