Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK), 40% Glass Fiber

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer Solvay Specialty Polymers
Trade Name AvaSpire®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK), 40% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire® AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK) designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical chemical resistance expected of PEEK while maintaining excellent elevated temperature properties.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Aircraft Applications; Electrical/Electronic Applications; Metal Replacement; SealsInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ASTM D792
Filler Content 40 %
40 %
Glass Fiber
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ISO 62
Viscosity 450000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
450000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.18 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm

@Thickness 3.18 mm
0.012 - 0.014 in/in

@Thickness 0.125 in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 380 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 716 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105
105
ASTM D785
Tensile Strength 191 MPa
27700 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 188 MPa

@Thickness 5.00 mm
27300 psi

@Thickness 0.197 in
5 mm/min, Type 1A; ISO 527-2
Elongation at Break 1.8 %
1.8 %
Type 1A, 5 mm/min; ISO 527-2
1.8 %
1.8 %
5 mm/min; ASTM D638
Tensile Modulus 15.1 GPa
2190 ksi
5 mm/min; ASTM D638
16.7 GPa
2420 ksi
1 mm/min, Type 1A; ISO 527-2
Flexural Strength 250 MPa
36300 psi
ISO 178
54.0 MPa

@Temperature 250 °C
7830 psi

@Temperature 482 °F
ASTM D790
253 MPa

@Temperature 23.0 °C
36700 psi

@Temperature 73.4 °F
ASTM D790
Flexural Modulus 14.8 GPa
2150 ksi
ASTM D790
15.4 GPa
2230 ksi
ISO 178
Compressive Strength 182 MPa
26400 psi
ASTM D695
Shear Strength 89.0 MPa
12900 psi
ASTM D732
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.90 J/cm
11.1 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
8.33 µin/in-°F

@Temperature -58.0 - 122 °F
1
Specific Heat Capacity 1.26 J/g-°C

@Temperature 50.0 °C
0.301 BTU/lb-°F

@Temperature 122 °F
ASTM C351
1.62 J/g-°C

@Temperature 200 °C
0.387 BTU/lb-°F

@Temperature 392 °F
ASTM C351
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 345 °C
653 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 285 °C
545 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 150 °C
302 °F
DSC
Flammability, UL94 V-1

@Thickness 0.800 mm
V-1

@Thickness 0.0315 in
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.80e+17 ohm-cm
1.80e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Constant 3.66

@Frequency 1.00e+6 Hz
3.66

@Frequency 1.00e+6 Hz
ASTM D150
3.68

@Frequency 60.0 Hz
3.68

@Frequency 60.0 Hz
ASTM D150
3.69

@Frequency 1000 Hz
3.69

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
ASTM D150
0.0020

@Frequency 60.0 Hz
0.0020

@Frequency 60.0 Hz
ASTM D150
0.0030

@Frequency 1.00e+6 Hz
0.0030

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 370 - 395 °C
698 - 743 °F
Mold Temperature 175 - 210 °C
347 - 410 °F
Drying Temperature 150 - 175 °C

@Time 9000 - 14400 sec
302 - 347 °F

@Time 2.50 - 4.00 hour
Back Pressure 0.138 - 0.345 MPa
20.0 - 50.0 psi
Screw Speed 75 rpm
75 rpm
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Natural
Form Pellets
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.0:1.0