Solvay Specialty Polymers AvaSpire® AV-722 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-722 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire AV-722 is an unreinforced polyaryletherketone (PAEK) that offers improved economics relative to PEEK while retaining most of PEEK's key performance attributes. AV-722 resin has been formulated for applications requiring high chemical resistance and mechanical strength along with low moisture absorption and good barrier properties. These and other properties make this resin well-suited for applications in healthcare, transportation, electronics, chemical processing and other industries. - Beige: AvaSpire AV-722 BG 20Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Viscosity 450000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
450000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.18 mm
0.0080 - 0.010 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125"; ASTM D955
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm

@Thickness 3.18 mm
0.012 - 0.014 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125"; ASTM D955
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
M-Scale; ASTM D785
Tensile Strength 89.0 MPa
12900 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 91.0 MPa
13200 psi
ISO 527-2/1A/50
Elongation at Break 25 %
25 %
50 mm/min; ASTM D638
25 %
25 %
ISO 527-2/1A/50
Elongation at Yield 4.5 %
4.5 %
ISO 527-2/1A/50
5.0 %
5.0 %
50 mm/min; ASTM D638
Tensile Modulus 3.70 GPa
537 ksi
50 mm/min; ASTM D638
3.90 GPa
566 ksi
ISO 527-2/1A/1
Flexural Strength 138 MPa
20000 psi
ISO 178
141 MPa
20500 psi
ASTM D790
Flexural Modulus 3.70 GPa
537 ksi
ASTM D790
3.80 GPa
551 ksi
ISO 178
Compressive Strength 112 MPa
16200 psi
ASTM D695
Poissons Ratio 0.43
0.43
ASTM E132
Shear Modulus 1.29 - 1.36 GPa
187 - 197 ksi
Calculated
Shear Strength 79.0 MPa
11500 psi
ASTM D732
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) NB
NB
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 45.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
25.0 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
Specific Heat Capacity 1.41 J/g-°C

@Temperature 50.0 °C
0.337 BTU/lb-°F

@Temperature 122 °F
DSC
1.97 J/g-°C

@Temperature 200 °C
0.471 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 340 °C
644 °F
Peak (major component); ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 161 °C

@Thickness 3.20 mm
322 °F

@Thickness 0.126 in
Annealed; 2 hours at 200°C; ASTM D648
Glass Transition Temp, Tg 150 °C
302 °F
ASTM D3418
Oxygen Index 40 %
40 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 3.10e+17 ohm-cm
3.10e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Constant 3.06

@Frequency 1.00e+6 Hz
3.06

@Frequency 1.00e+6 Hz
ASTM D150
3.12

@Frequency 60.0 Hz
3.12

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm

@Thickness 3.00 mm
483 kV/in

@Thickness 0.118 in
ASTM D149
170 kV/mm

@Thickness 0.0500 mm
4320 kV/in

@Thickness 0.00197 in
Amorphous Film; ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
ASTM D150
0.0040

@Frequency 1.00e+6 Hz
0.0040

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 354 °C
669 °F
Middle Barrel Temperature 366 °C
691 °F
Front Barrel Temperature 371 °C
700 °F
Nozzle Temperature 374 °C
705 °F
Mold Temperature 177 - 204 °C
351 - 399 °F
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Beige
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Ductile
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Impact Resistance
High Heat Resistance
Forms Pellets
Generic PAEK
Injection Rate Fast
Processing Method Extrusion Blow Molding
Fiber (Spinning) Extrusion
Film Extrusion
Injection Blow Molding
Injection Molding
Machining
Profile Extrusion
Thermoforming
Wire & Cable Extrusion
Screw Compression Ratio 2.5:1.0 to 3.5:1.0
Uses Aircraft Applications
Automotive Applications
Electrical/Electronic Applications
Film
Fuel Lines
Gears
Medical/Healthcare Applications
Oil/Gas Applications
Seals