Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 resin. This resin offers chemical resistance nearly equivalent to glass fiber-reinforced PEEK in most chemicals, with a lower heat deflection temperature. These properties make it well suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. - Beige: AvaSpire AV-651 GF30 BG 20 - Black: AvaSpire AV-651 GF30 BK 95Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Filler Content 30 %
30 %
Glass Fiber Reinforcement
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ASTM D570
Viscosity 410000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
410000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt; ASTM D3835
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.18 mm
0.0020 - 0.0040 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse 0.013 - 0.015 cm/cm

@Thickness 3.18 mm
0.013 - 0.015 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 101
101
M-Scale; ASTM D785
Tensile Strength 156 MPa
22600 psi
5.0 mm/min; ASTM D638
Tensile Strength, Yield 162 MPa
23500 psi
5 nm; ISO 527-2/1A/5
Elongation at Break 2.9 %
2.9 %
5.0 mm/min; ASTM D638
2.9 %
2.9 %
ISO 527-2/1A/5
Tensile Modulus 9.90 GPa
1440 ksi
5.0 mm/min; ASTM D638
10.4 GPa
1510 ksi
ISO 527-2/1A/1
Flexural Strength 228 MPa
33100 psi
ISO 178
234 MPa
33900 psi
ASTM D790
Flexural Modulus 9.40 GPa
1360 ksi
ASTM D790
9.70 GPa
1410 ksi
ISO 178
Compressive Strength 168 MPa
24400 psi
ASTM D695
Shear Strength 82.6 MPa
12000 psi
ASTM D732
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
9.60 J/cm
18.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 64.0 kJ/m²
30.5 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
9.44 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
Specific Heat Capacity 1.27 J/g-°C

@Temperature 50.0 °C
0.304 BTU/lb-°F

@Temperature 122 °F
DSC
1.65 J/g-°C

@Temperature 200 °C
0.394 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 345 °C
653 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
ASTM D3418
Flammability, UL94 V-1

@Thickness 0.800 mm
V-1

@Thickness 0.0315 in
UL 94
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Constant 3.58

@Frequency 1.00e+6 Hz
3.58

@Frequency 1.00e+6 Hz
ASTM D150
3.61

@Frequency 60.0 Hz
3.61

@Frequency 60.0 Hz
ASTM D150
3.63

@Frequency 1000 Hz
3.63

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm

@Thickness 3.00 mm
432 kV/in

@Thickness 0.118 in
ASTM D149
Dissipation Factor 0.0020

@Frequency 60.0 Hz
0.0020

@Frequency 60.0 Hz
ASTM D150
0.0040

@Frequency 1.00e+6 Hz
0.0040

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 365 °C
689 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 366 - 388 °C
691 - 730 °F
Mold Temperature 160 - 190 °C
320 - 374 °F
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Agency Ratings ISO 10993
ISO 10993-Part 1
Appearance Beige
Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Autoclave Sterilizable
Biocompatible
E-beam Sterilizable
Ethylene Oxide Sterilizable
Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Sterilizability
Heat Sterilizable
High Heat Resistance
High Stiffness
High Strength
Radiation (Gamma) Resistant
Radiation Sterilizable
Radiotranslucent
Steam Resistant
Steam Sterilizable
Forms Pellets
Generic PAEK
Injection Rate Fast
Processing Method Injection Molding
Machining
Profile Extrusion
Screw Compression Ratio 2.0:1.0 to 3.0:1.0
Uses Aircraft Applications
Connectors
Dental Applications
Electrical/Electronic Applications
Film
Hospital Goods
Industrial Applications
Medical Appliances
Medical/Healthcare Applications
Seals
Surgical Instruments