Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire AV-651 CF30 is a 30% carbon fiber reinforced version of AvaSpire AV-651. This formulation offers some advantages relative to 30% carbon fiber reinforced PEEK which include better dimensional stability and warp resistance during injection molding. The AV-651 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-651-based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-651 CF30 makes this grade well suited for a broad range of applications across a number of industries including healthcare, transportation, electronics, oil and gas, and chemical processing. This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-651 CF30 is overall very similar to that of 30% CF reinforced PEEK. While the resin can also be extruded, the lower melt flow AV-621 CF30 grade is considered more suited for extrusion applications while offering the same property profile as AV-651 CF30.Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Filler Content 30 %
30 %
Carbon Fiber Reinforcement
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ASTM D570
Viscosity 540000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
540000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt; ASTM D3835
Linear Mold Shrinkage, Flow 0.00 - 0.0020 cm/cm

@Thickness 3.18 mm
0.00 - 0.0020 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Thickness 3.18 mm
0.0090 - 0.011 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow 4.5 g/10 min

@Load 2.16 kg,
Temperature 400 °C
4.5 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 104
104
M-Scale; ASTM D785
Tensile Strength 184 MPa
26700 psi
5.0 mm/min; ASTM D638
Tensile Strength, Yield 192 MPa
27800 psi
ISO 527-2/1A/5
Elongation at Break 1.5 %
1.5 %
5.0 mm/min; ASTM D638
1.5 %
1.5 %
ISO 527-2/1A/5
Tensile Modulus 20.7 GPa
3000 ksi
5.0 mm/min; ASTM D638
21.1 GPa
3060 ksi
ISO 527-2/1A/1
Flexural Strength 262 MPa
38000 psi
ASTM D790
280 MPa
40600 psi
ISO 178
Flexural Modulus 17.2 GPa
2490 ksi
ASTM D790
19.1 GPa
2770 ksi
ISO 178
Compressive Strength 168 MPa
24400 psi
ASTM D695
Shear Strength 94.0 MPa
13600 psi
ASTM D732
Izod Impact, Notched 0.590 J/cm
1.11 ft-lb/in
ASTM D256
5.90 J/cm
11.1 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.40 kJ/m²
4.00 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 8.20 µm/m-°C

@Temperature -50.0 - 50.0 °C
4.56 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
Specific Heat Capacity 1.32 J/g-°C

@Temperature 50.0 °C
0.315 BTU/lb-°F

@Temperature 122 °F
DSC
1.77 J/g-°C

@Temperature 200 °C
0.423 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 345 °C
653 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 212 °C

@Thickness 3.20 mm
414 °F

@Thickness 0.126 in
Annealed; 2 hours at 200°C; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
ASTM D3418
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 366 - 388 °C
691 - 730 °F
Mold Temperature 149 - 177 °C
300 - 351 °F
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Autoclave Sterilizable
E-beam Sterilizable
Ethylene Oxide Sterilizable
Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Sterilizability
Heat Sterilizable
High Heat Resistance
High Stiffness
High Strength
Radiation (Gamma) Resistant
Radiation Sterilizable
Radiotranslucent
Steam Resistant
Steam Sterilizable
Forms Pellets
Generic PAEK
Injection Rate Fast
Processing Method Injection Molding
Machining
Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.0:1.0 to 3.0:1.0
Uses Dental Applications
Hospital Goods
Medical Appliances
Medical/Healthcare Applications
Pump Parts
Seals
Surgical Instruments