Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.125 in (3 mm).Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; Heat Stabilized; High Heat Resistance; High Strength; Low Moisture AbsorptionUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Connectors; Fuel Lines; General Purpose; Housings; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Oil/Gas Applications; Power/Other Tools; Thick-walled Parts; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D4000 PA121 G35 Color: BK324 Black; ASTM D4000 PA121 G35 Color: NT Natural; ASTM D4000 PPA0111 G33 GB145 KD200 KN090 PN080 YI265 Color: BK324 Black; ASTM D4000 PPA0111 G33 GB145 KD200 KN090 PN080 YI265 Color: NT Natural; ASTM D6779 PA121G35; BOSCH N28 BN05-OX1 BN0510-GF35-3Anf01SO Color: NT Natural; BOSCH N28 BN05-OX1 BN0510-GF35-3Asw01SO Color: BK324 Black; DELPHI M-6071 Color: NT Natural; FORD WSK-M4D843-A2 Color: BK324 Black; FORD WSK-M4D843-A2 Color: NT Natural; ISO 1874 PA6T/6I/66, MH, 12-120, GF33 Color: BK324 Black; ISO 1874 PA6T/6I/66, MH, 12-120, GF33 Color: NT Natural; SIEMENS S219536 Color: NT NaturalInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
Dry; ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Linear Mold Shrinkage, Flow 0.00 cm/cm
0.00 in/in
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 193 MPa
28000 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ASTM D638
Tensile Modulus 13.1 GPa
1900 ksi
ASTM D638
Flexural Yield Strength 254 MPa
36800 psi
ASTM D790
Flexural Modulus 10.3 GPa
1490 ksi
ASTM D790
Compressive Strength 247 MPa
35800 psi
ASTM D695
Shear Strength 88.9 MPa
12900 psi
ASTM D732
Izod Impact, Notched 0.750 J/cm
1.41 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
Peak; Dry; ASTM D3418
310 °C
590 °F
Dry; ISO 11357-3
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+15 ohm-cm
2.00e+15 ohm-cm
ASTM D257
Dielectric Constant 4.3

@Frequency 1.00e+6 Hz
4.3

@Frequency 1.00e+6 Hz
ASTM D150
4.7

@Frequency 60.0 Hz
4.7

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 3.20 mm
533 kV/in

@Thickness 0.126 in
ASTM D149
Dissipation Factor 0.0090

@Frequency 60.0 Hz
0.0090

@Frequency 60.0 Hz
ASTM D150
0.022

@Frequency 1.00e+6 Hz
0.022

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 120 sec
120 sec
ASTM D495
Comparative Tracking Index 550 V
550 V
UL 746
Processing Properties Metric English Comments
Processing Temperature 79.4 °C
175 °F
Hopper
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Natural
Form Pellets
Processing Technique Injection Molding