Solvay Specialty Polymers Amodel® AE-8133 Polyphthalamide (PPA) (discontinued **)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® AE-8133 Polyphthalamide (PPA) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel AE-8133 is a 33% glass reinforced polyphthalamide (PPA) designed to work in the modern automotive electrical environment. This grade features a high heat deflection temperature, high flexural modulus and high tensile strength, as well as excellent creep resistance and low moisture absorption. - Black: AE-8133 BK902 - Natural: AE-8133 NTInjection Notes: Injection Rate: 3-4 inch/second (7.5-10 cm/sec) Holding Pressure: 50% of injection pressureData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.49 g/cc	0.0538 lb/in³	ISO 1183/A
Filler Content	33 %	33 %	Glass Fiber Reinforcement
Water Absorption	0.16 % @Time 86400 sec	0.16 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190 MPa @Temperature 23.0 °C	27600 psi @Temperature 73.4 °F	ISO 527-2
Elongation at Break	1.7 % @Temperature 23.0 °C	1.7 % @Temperature 73.4 °F	ISO 527-2
Tensile Modulus	13.6 GPa @Temperature 23.0 °C	1970 ksi @Temperature 73.4 °F	ISO 527-2
Flexural Strength	290 MPa @Temperature 23.0 °C	42100 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	11.9 GPa @Temperature 23.0 °C	1730 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	8.20 kJ/m²	3.90 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	45.0 kJ/m² @Temperature 23.0 °C	21.4 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	5.40 J/cm²	25.7 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	24.0 µm/m-°C @Temperature 0.000 - 100 °C	13.3 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
	27.0 µm/m-°C @Temperature 100 - 200 °C	15.0 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	55.0 µm/m-°C @Temperature 0.000 - 100 °C	30.6 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	110 µm/m-°C @Temperature 100 - 200 °C	61.1 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
Melting Point	325 °C	617 °F	ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi)	295 °C	563 °F	Unannealed; ISO 75-2/A
Glass Transition Temp, Tg	135 °C	275 °F	DSC
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+15 ohm-cm	2.00e+15 ohm-cm	Conditioned; ASTM D257
	4.90e+15 ohm-cm	4.90e+15 ohm-cm	ASTM D257
Dielectric Constant	4.02 @Frequency 1.00e+6 Hz	4.02 @Frequency 1.00e+6 Hz	ASTM D150
	4.3 @Frequency 1.00e+6 Hz	4.3 @Frequency 1.00e+6 Hz	Conditioned; ASTM D150
	4.35 @Frequency 60.0 Hz	4.35 @Frequency 60.0 Hz	ASTM D150
	4.7 @Frequency 60.0 Hz	4.7 @Frequency 60.0 Hz	Conditioned; ASTM D150
Dielectric Strength	18.0 kV/mm @Thickness 3.20 mm	457 kV/in @Thickness 0.126 in	Conditioned; ASTM D149
	18.0 kV/mm @Thickness 3.20 mm	457 kV/in @Thickness 0.126 in	ASTM D149
Dissipation Factor	0.0070 @Frequency 60.0 Hz	0.0070 @Frequency 60.0 Hz	ASTM D150
	0.0090 @Frequency 60.0 Hz	0.0090 @Frequency 60.0 Hz	Conditioned; ASTM D150
	0.016 @Frequency 1.00e+6 Hz	0.016 @Frequency 1.00e+6 Hz	ASTM D150
	0.022 @Frequency 1.00e+6 Hz	0.022 @Frequency 1.00e+6 Hz	Conditioned; ASTM D150
Arc Resistance	120 sec	120 sec	Conditioned; ASTM D495
	140 sec	140 sec	ASTM D495
Comparative Tracking Index	600 V	600 V	Conditioned; UL 746
	600 V	600 V	UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	316 - 330 °C	601 - 626 °F
Middle Barrel Temperature	316 - 330 °C	601 - 626 °F
Front Barrel Temperature	324 - 340 °C	615 - 644 °F
Melt Temperature	330 - 352 °C	626 - 666 °F
Mold Temperature	150 - 165 °C	302 - 329 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.030 - 0.060 %	0.030 - 0.060 %

Descriptive Properties	Value	Comments
Appearance	Black
	Natural Color
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Stiffness
	High Heat Resistance
	High Stiffness
	High Strength
	High Temperature Strength
	Low Moisture Absorption
Flexural Strain (%)	2.5
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
Uses	Automotive Electronics
	Connectors
	Electrical Parts
	Electrical/Electronic Applications