Solvay Specialty Polymers Amodel® AE-4133 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AE-4133 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AE-4133 is a 33% glass reinforced, hot-water moldable polyphthalamide (PPA) designed to work in the modern automotive electrical environment. This grade features a high heat deflection temperature, high flexural modulus and high tensile strength, as well as excellent creep resistance and low moisture absorption. - Black: AE-4133 BK902 - Natural: AE-4133 NTInjection Notes: Injection Rate: 3-4 inch/second (7.5-10 cm/sec) Holding Pressure: 50% of injection pressureData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183/A
Filler Content 33 %
33 %
Glass Fiber Reinforcement
Water Absorption 0.23 %

@Time 86400 sec
0.23 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa

@Temperature 23.0 °C
30500 psi

@Temperature 73.4 °F
ISO 527-2
Elongation at Break 2.5 %

@Temperature 23.0 °C
2.5 %

@Temperature 73.4 °F
ISO 527-2
Tensile Modulus 12.0 GPa

@Temperature 23.0 °C
1740 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 295 MPa

@Temperature 23.0 °C
42800 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 10.7 GPa

@Temperature 23.0 °C
1550 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 9.20 kJ/m²
4.38 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 68.0 kJ/m²

@Temperature 23.0 °C
32.4 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 7.90 J/cm²
37.6 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature 100 - 200 °C
8.33 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
20.0 µm/m-°C

@Temperature 0.000 - 100 °C
11.1 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 76.0 µm/m-°C

@Temperature 0.000 - 100 °C
42.2 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
120 µm/m-°C

@Temperature 100 - 200 °C
66.7 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Melting Point 327 °C
621 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) >= 300 °C
>= 572 °F
Unannealed; ISO 75-2/A
Glass Transition Temp, Tg 95.0 °C
203 °F
DSC
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+14 ohm-cm
5.00e+14 ohm-cm
Conditioned; ASTM D257
5.60e+15 ohm-cm
5.60e+15 ohm-cm
ASTM D257
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
3.75

@Frequency 1.00e+6 Hz
3.75

@Frequency 1.00e+6 Hz
ASTM D150
4.1

@Frequency 60.0 Hz
4.1

@Frequency 60.0 Hz
ASTM D150
4.3

@Frequency 60.0 Hz
4.3

@Frequency 60.0 Hz
Conditioned; ASTM D150
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
483 kV/in

@Thickness 0.126 in
Conditioned; ASTM D149
19.0 kV/mm

@Thickness 3.20 mm
483 kV/in

@Thickness 0.126 in
ASTM D149
Dissipation Factor 0.0060

@Frequency 60.0 Hz
0.0060

@Frequency 60.0 Hz
ASTM D150
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
ASTM D150
0.019

@Frequency 1.00e+6 Hz
0.019

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
0.020

@Frequency 60.0 Hz
0.020

@Frequency 60.0 Hz
Conditioned; ASTM D150
Comparative Tracking Index 600 V
600 V
UL 746
600 V
600 V
Conditioned; UL 746
High Voltage Arc-Tracking Rate, HVTR 14.0 mm/min
0.551 in/min
UL 746
18.0 mm/min
0.709 in/min
Conditioned; UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 320 - 330 °C
608 - 626 °F
Middle Barrel Temperature 320 - 330 °C
608 - 626 °F
Front Barrel Temperature 327 - 335 °C
621 - 635 °F
Melt Temperature 330 - 345 °C
626 - 653 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Descriptive Properties Value Comments
Appearance Black
Natural Color
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Stiffness
High Heat Resistance
High Stiffness
High Strength
High Temperature Strength
Low Moisture Absorption
Flexural Strain (%) 3.1
Forms Pellets
Generic PPA
Processing Method Injection Molding
Uses Automotive Electronics
Connectors
Electrical Parts
Electrical/Electronic Applications