- Solvay Specialty Polymers Amodel® AE-4133 Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Solvay Specialty Polymers Amodel® AE-4133 Polyphthalamide (PPA), 33% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® AE-4133 Polyphthalamide (PPA), 33% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® AE-4133 is a 33% glass reinforced, hot-water moldable polyphthalamide (PPA) designed to work in the modern automotive electrical environment. Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Stiffness; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Automotive Electronics; Connectors; Electrical Parts; Electrical/Electronic ApplicationsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Additional Properties: Flexural Strain - ISO 178 3.1 %Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Water Absorption | 0.23 % @Time 86400 sec |
0.23 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 210 MPa | 30500 psi | ISO 527-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-2 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-2 |
| Flexural Strength | 295 MPa | 42800 psi | ISO 178 |
| Flexural Modulus | 10.7 GPa | 1550 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.20 kJ/m² | 4.38 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 7.90 J/cm² | 37.6 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 100 - 200 °C |
8.33 µin/in-°F @Temperature 212 - 392 °F |
2 |
| 20.0 µm/m-°C @Temperature 0.000 - 100 °C |
11.1 µin/in-°F @Temperature 32.0 - 212 °F |
2 | |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature 0.000 - 100 °C |
42.2 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 120 µm/m-°C @Temperature 100 - 200 °C |
66.7 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 327 °C | 621 °F | ISO 11357-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Unannealed; ISO 75-2/A |
| Glass Transition Temp, Tg | 95.0 °C | 203 °F | DSC |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.60e+15 ohm-cm | 5.60e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.75 @Frequency 1.00e+6 Hz |
3.75 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 4.1 @Frequency 60.0 Hz |
4.1 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 60.0 Hz |
0.0060 @Frequency 60.0 Hz |
ASTM D150 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| High Voltage Arc-Tracking Rate, HVTR | 14.0 mm/min | 0.551 in/min | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 320 - 330 °C | 608 - 626 °F | |
| Middle Barrel Temperature | 320 - 330 °C | 608 - 626 °F | |
| Front Barrel Temperature | 327 - 335 °C | 621 - 635 °F | |
| Melt Temperature | 330 - 345 °C | 626 - 653 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Suggested Max |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- SPHERE ONE EXTENDOSPHERESâ„¢ XOL-150 Hollow Spheres
- Techmer ES Plaslube® NY-1/TF/15 NAT PA66
- SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA
- Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH0
- Wellman Wellamid® GFT1702-WBK1 33% Glass Fiber Reinforced, Impact Modified and Weatherable Nylon 66
- Wieland 1925 Wilaform Palladium
- Toyobo VYLOPET® EMC355 Injection Molding Polyester Resin, Glass Reinforced
- Hexcel® Redux® 610W (0.09 psf) Flame retarded epoxy film adhesive
- Master Bond Supreme 3AN One Component, Heat Curing Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved