Solvay Specialty Polymers Amodel® A-8950 HS Polyphthalamide (PPA), 50% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-8950 HS Polyphthalamide (PPA), 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® A-8950 HS is a 50% glass-fiber-reinforced, heat-stabilized polyphthalamide (PPA) with a high heat deflection temperature and very high tensile strength. Excellent creep resistance, low moisture absorption and glycol resistance are also characteristic of this resin.Features: Glycol Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Stiffness; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Appliances; Automotive Applications; Automotive Electronics; Connectors; Consumer Applications; Housings; Industrial Applications; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 275 MPa
39900 psi
ISO 527-2
Elongation at Break 2.1 %
2.1 %
ISO 527-2
Tensile Modulus 19.0 GPa
2760 ksi
ISO 527-2
Charpy Impact Unnotched 7.50 J/cm²
35.7 ft-lb/in²
Type 1, Edgewise; ISO 179
Charpy Impact, Notched 1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
Type 1, Edgewise; ISO 179
1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Melting Point 325 °C
617 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 310 °C
590 °F
HDT B; Unannealed; Flatwise; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 295 °C
563 °F
Unannealed; Flatwise; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 316 - 329 °C
601 - 624 °F
Middle Barrel Temperature 316 - 329 °C
601 - 624 °F
Front Barrel Temperature 324 - 335 °C
615 - 635 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 150 °C
302 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Suggested Max
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding