Solvay Specialty Polymers Amodel® A-6135 NL Polyphthalamide (PPA), 35% Glass Fiber Reinforcement  (discontin

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-6135 NL Polyphthalamide (PPA), 35% Glass Fiber Reinforcement  (discontin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel A-6135 NL polyphthalamide (PPA), a 35% glass reinforced, high-glow, non-lubricated, hot-water moldable resin specially designed for laser welding. The black version is a laser absorber, and the natural is laser transmissive. - Black: A-6135 NL BK543- Natural: A-6135 NL NTFeatures: Good Chemical Resistance; Good Creep Resistance; Good Flow; Good Stiffness; High Stiffness; High Strength; Hot Water Moldability; Laser Weldable; Low Moisture AbsorptionUses: Automotive Applications; Automotive Electronics; Connectors; Electrical Parts; HousingsAvailability: Africa & Middle East; Asia Pacific; Europe; North America; South AmericaInjection Rate: 3 to 6 in/secHolding Pressure: 50% of injection pressureInformation provide by Solvay Specialty Polymers
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183 Method A
Water Absorption 0.29 %
0.29 %
24 hrs; ISO 62
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
flow; ISO 294-4
0.010 cm/cm
0.010 in/in
across flow; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 220 MPa
31900 psi
ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
Tensile Modulus 12.5 GPa
1810 ksi
ISO 527-2
Flexural Strength 300 MPa
43500 psi
3.5%; ISO 178
Flexural Modulus 11.4 GPa
1650 ksi
ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 65.0 kJ/m²
30.9 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 303 °C
577 °F
Unannealed; Flatwise; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 288 °C
550 °F
Unannealed; Flatwise; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 315 - 321 °C
599 - 610 °F
Middle Barrel Temperature 315 - 321 °C
599 - 610 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 320 - 335 °C
608 - 635 °F
Mold Temperature 65.0 - 93.0 °C
149 - 199 °F
Drying Temperature 120 °C
248 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
suggested max
Descriptive Properties Value Comments
Appearance Black; Natural Color
Forms Pellets
Processing Method Water-Assisted Injection Molding
RoHS Compliance Contact Manufacturer