Solvay Specialty Polymers Amodel® A-1945 HSL Polyphthalamide (PPA) (discontinued **)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1945 HSL Polyphthalamide (PPA) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel A-1945 HSL is a 45% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material was tested using the aggressive automotive coolant system, ethylene glycol with organic acid stabilizer, at 130°C (266°F). It exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze. Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets, and valves. - Black: A-1945 HSL BK 328Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.58 g/cc	0.0571 lb/in³	ISO 1183/A
Filler Content	45 %	45 %	Glass Fiber Reinforcement
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	Type D2; ASTM D955
	0.0010 cm/cm	0.0010 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	Type D2; ASTM D955
	0.0060 cm/cm	0.0060 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	124	124	R-Scale; ASTM D785
Tensile Strength	151 MPa	21900 psi	67% Retained; After Immersion in Glycol Solution (50% Valvoline Zerex® G-05 and 50% water) for 1,000 hours at 130°C (266°F).; ASTM D638
	226 MPa	32800 psi	ASTM D638
Elongation at Break	2.0 %	2.0 %	ISO 527-2
Tensile Modulus	13.9 GPa	2020 ksi	ISO 527-2
Flexural Strength	302 MPa	43800 psi	ISO 178
Flexural Modulus	12.5 GPa	1810 ksi	ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/m²	4.28 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.970 J/cm²	4.62 ft-lb/in²	ISO 179/1eA
	1.10 J/cm²	5.23 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	323 °C	613 °F	ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi)	299 °C	570 °F	Unannealed; ISO 75-2/A

Processing Properties	Metric	English
Rear Barrel Temperature	304 - 318 °C	579 - 604 °F
Front Barrel Temperature	316 - 329 °C	601 - 624 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	150 °C	302 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
	Lubricant
	Mold Release
Appearance	Black
Automotive Specifications	ASTM D6779 PA131G45
	ISO 1874-PA6T/6I, MH, 11-160, GF45 Color: BK-328 and NT-07 Black and Natural
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Antifreeze Resistant
	Glycol Resistant
	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Stiffness
	High Heat Resistance
	High Strength
	Lubricated
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Automotive Under the Hood
	Housings
	Machine/Mechanical Parts
	Valves/Valve Parts