Solvay Specialty Polymers Amodel® A-1240 HS Polyphthalamide (PPA) Resin, 40% Mineral Reinforced, Dry As Molded &nbs

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-1240 HS Polyphthalamide (PPA) Resin, 40% Mineral Reinforced, Dry As Molded &nbs.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL A-1240 polyphthalamide (PPA) resins are 40% mineral filled resins that have high deflection temperature, flexural modulus, and tensile strength. They mold with low warpage, have excellent dimensional stability and low moisture absorption. There are two versions of AMODEL A-1240 resin, "L" and "HS". The L version will usually provide the smoother, higher gloss surface, while the HS version gives better long-term thermal aging properties. Both AMODEL A-1240 resins can be easily processed using conventional equipment and methods.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.MatWeb has an entry for this material conditioned at 50% RH.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ASTM D792
Water Absorption 0.14 %
0.14 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM E831
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ASTM E831
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
ASTM D785
Tensile Strength, Ultimate 110 MPa
16000 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ASTM D638
Tensile Modulus 9.00 GPa
1310 ksi
ASTM D638
Flexural Yield Strength 207 MPa
30000 psi
ASTM D790
Flexural Modulus 7.60 GPa
1100 ksi
ASTM D790
Poissons Ratio 0.29
0.29
Shear Modulus 3.49 GPa
506 ksi
Calculated
Shear Strength 96.0 MPa
13900 psi
ASTM D732
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.30 J/cm
9.93 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 34.0 µm/m-°C

@Temperature 0.000 - 100 °C
18.9 µin/in-°F

@Temperature 32.0 - 212 °F
FD; ASTM E831
79.0 µm/m-°C

@Temperature 160 - 250 °C
43.9 µin/in-°F

@Temperature 320 - 482 °F
FD; ASTM E831
95.0 µm/m-°C

@Temperature 160 - 250 °C
52.8 µin/in-°F

@Temperature 320 - 482 °F
TD; ASTM E831
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature 0.000 - 100 °C
22.2 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E381
Melting Point 310 °C
590 °F
ASTM D3418
Maximum Service Temperature, Air 140 °C
284 °F
20,000 hours continuous use; ASTM D3045
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 154 °C
309 °F
ASTM D648
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity 9.00e+15 ohm-cm
9.00e+15 ohm-cm
ASTM D257
Dielectric Constant 4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
ASTM D150
4.2

@Frequency 100 Hz
4.2

@Frequency 100 Hz
ASTM D150
Dissipation Factor 0.0060

@Frequency 100 Hz
0.0060

@Frequency 100 Hz
ASTM D150
0.017

@Frequency 1e+6 Hz
0.017

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 125 sec
125 sec
ASTM D495
Comparative Tracking Index 550 V
550 V
Processing Properties Metric English Comments
Melt Temperature 321 - 343 °C
610 - 649 °F
Injection