Solvay Specialty Polymers Amodel® A-1230 L Polyphthalamide (PPA) (discontinued **)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1230 L Polyphthalamide (PPA) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel A-1230 L is a 30% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and tensile strength, and low moisture absorption. - Black: A-1230 L BK 324Additional Information: Continuous Use Temperature, ASTM D3045, 5000 hrs: 311°F Continuous Use Temperature, ASTM D3045, 20000 hrs: 275°FData is presented for dry polymer.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.45 g/cc	0.0524 lb/in³	ISO 1183/A
Filler Content	30 %	30 %	Mineral Filler
Water Absorption	0.12 % @Time 86400 sec	0.12 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.011 cm/cm	0.011 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	126	126	R-Scale; ASTM D785
Tensile Strength, Yield	95.8 MPa	13900 psi	ISO 527-2
	104 MPa	15100 psi	ASTM D638
Elongation at Break	1.6 %	1.6 %	ASTM D638
	1.6 %	1.6 %	ISO 527-2
Tensile Modulus	6.89 GPa	999 ksi	ISO 527-2
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Flexural Modulus	6.21 GPa	901 ksi	ASTM D790
Compressive Strength	152 MPa	22000 psi	ASTM D695
Poissons Ratio	0.31	0.31	ASTM E132
Shear Modulus	2.63 GPa	381 ksi	Calculated
Shear Strength	81.4 MPa	11800 psi	ASTM D732
Izod Impact, Notched	0.430 J/cm	0.806 ft-lb/in	ASTM D256
Charpy Impact Unnotched	2.50 J/cm²	11.9 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.210 J/cm²	0.999 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	41.0 µm/m-°C @Temperature 0.000 - 100 °C	22.8 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
	88.0 µm/m-°C @Temperature 160 - 249 °C	48.9 µin/in-°F @Temperature 320 - 480 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	49.0 µm/m-°C @Temperature 0.000 - 100 °C	27.2 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	110 µm/m-°C @Temperature 160 - 249 °C	61.1 µin/in-°F @Temperature 320 - 480 °F	ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	279 °C	534 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	158 °C	316 °F	Unannealed; ASTM D648
Flammability, UL94	HB @Thickness 3.18 mm	HB @Thickness 0.125 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	ASTM D150
	4.2 @Frequency 60.0 Hz	4.2 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	21.0 kV/mm @Thickness 3.18 mm	533 kV/in @Thickness 0.125 in	ASTM D149
Dissipation Factor	0.0060 @Frequency 60.0 Hz	0.0060 @Frequency 60.0 Hz	ASTM D150
	0.018 @Frequency 1.00e+6 Hz	0.018 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	125 sec	125 sec	ASTM D495
Comparative Tracking Index	550 V	550 V	UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	304 - 318 °C	579 - 604 °F
Front Barrel Temperature	316 - 329 °C	601 - 624 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	135 °C	275 °F
Drying Temperature	120 °C	248 °F
Dry Time	2.50 hour	2.50 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Lubricant
	Mold Release
Appearance	Black
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Low Moisture Absorption
	Low Warpage
	Lubricated
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Electrical/Electronic Applications
	Industrial Applications