Solvay Specialty Polymers Amodel® A-1133 NL WH 505 Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1133 NL WH 505 Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel A-1133 NL resin is a 33% glass reinforced polyphthalamide (PPA) which is distinguished by its high-reflectivity white color. This grade features a high deflection temperature for compatibility with SMT processes, and low moisture absorption. - White: A-1133 NL WH 505Injection Notes: A general purpose screw is recommended, with minimum back pressure.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.54 g/cc	0.0556 lb/in³	ISO 1183/A
Filler Content	33 %	33 %	Glass Fiber Reinforcement
Water Absorption	0.16 % @Time 86400 sec	0.16 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	125	125	R-Scale; ASTM D785
Tensile Strength at Break	179 MPa	26000 psi	ASTM D638
Elongation at Break	1.8 %	1.8 %	ASTM D638
Tensile Modulus	12.4 GPa	1800 ksi	ASTM D638
Flexural Yield Strength	236 MPa	34200 psi	ASTM D790
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
Poissons Ratio	0.41	0.41	ASTM E132
Shear Modulus	4.40 GPa	638 ksi	Calculated
Izod Impact, Notched	0.370 J/cm	0.693 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	14.0 µm/m-°C @Temperature 160 - 249 °C	7.78 µin/in-°F @Temperature 320 - 480 °F	TMA; ASTM E831
	23.0 µm/m-°C @Temperature 0.000 - 100 °C	12.8 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	4.50 µm/m-°C @Temperature 0.000 - 100 °C	2.50 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	100 µm/m-°C @Temperature 160 - 249 °C	55.6 µin/in-°F @Temperature 320 - 480 °F	ASTM E831
Melting Point	310 °C	590 °F	ASTM D570
Deflection Temperature at 1.8 MPa (264 psi)	271 °C	520 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	304 - 318 °C	579 - 604 °F
Front Barrel Temperature	316 - 329 °C	601 - 624 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	135 °C	275 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Appearance	White
Automotive Specifications	ASTM D6779 PA128G35
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Color Stability
	High Reflectivity
	Low Moisture Absorption
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
Uses	Automotive Electronics
	Housings
	LEDs