| Category | Polymer , Film , Thermoplastic , Polyphenylsulfone (PPSU) |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Ajedium™ Films -- Radel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ajedium™ Films -- Radel® R-5100 NT15 Polyphenylsulfone (PPSU).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Radel® polyphenylsulfone is an amorphous thermoplastic material that offers exceptional hydrolytic stability, and toughness superior to other commercially available, high-temperature films. PPSU films have high deflection temperatures and outstanding resistance to environmental stress cracking. The polymer is inherently flame retardant. The excellent thermal stability makes films suitable for applications where very low shrink at high temperatures are needed. PPSU films also have good electrical properties.Features: Flame Retardant; Good Electrical Properties; Good Thermal Stability; Good Toughness; High ESCR (Stress Crack Resist.); Hydrolytically StableUses: Aerospace Applications; Aircraft Applications; Automotive Applications; Batteries; Electrical/Electronic Applications; Food Service Applications; Medical/Healthcare ApplicationsAdditional Properties: Area Factor - 149 ft²/lb/milInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.37 % @Time 86400 sec |
0.37 % @Time 24.0 hour |
ISO 62 |
| Thickness | 25.0 microns | 0.984 mil | As Tested |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 68.0 MPa | 9860 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 59.0 MPa | 8560 psi | ASTM D882 |
| Film Elongation at Break, MD | 140 % | 140 % | ASTM D882 |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882 |
| Film Elongation at Yield, MD | 9.2 % | 9.2 % | ASTM D882 |
| Film Elongation at Yield, TD | 6.8 % | 6.8 % | ASTM D882 |
| Secant Modulus, MD | 1.59 GPa | 231 ksi | ASTM D882 |
| Secant Modulus, TD | 1.98 GPa | 287 ksi | ASTM D882 |
| Dart Drop Test | 540 g | 1.19 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 92.0 MPa | 13300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 70.0 MPa | 10200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 56.0 µm/m-°C @Thickness 3.18 mm |
31.1 µin/in-°F @Thickness 0.125 in |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 220 °C | 428 °F | ASTM E1356 |
| Oxygen Index | 38 % | 38 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+15 ohm-cm | 9.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 1.38 | 1.38 | ASTM D150 |
| Dielectric Strength | 190 kV/mm @Thickness 0.0250 mm |
4830 kV/in @Thickness 0.000984 in |
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Opaque | |
| RoHS Compliance | RoHS Compliant |