Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyketone, Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1130 is a 30 percent glass fiber reinforced compound based on a developmental engineering polyketone resin available in natural and black from Shell Chemical Company. Due to the base polymer's balance of stiffness, toughness and chemical resistance coupled with its easy processing, this compound is expected to find application in the appliance, automotive, electrical and other industries.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Water Absorption 0.42 %
0.42 %
24 hour immersion; ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Ultimate 130 MPa
18900 psi
ASTM D638
Elongation at Break 3.1 %
3.1 %
ASTM D638
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Flexural Strength 200 MPa
29000 psi
at 5% strain; ASTM D790
Flexural Modulus 7.20 GPa
1040 ksi
ASTM D790
Izod Impact, Notched 0.850 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
1.59 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
ASTM D256
1.40 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.62 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Taber Abrasion, mg/1000 Cycles 42
42
1 kg load; CS-17 Wheel; ASTM D1044
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 218 °C
424 °F
ASTM D648
Vicat Softening Point 215 °C
419 °F
ASTM D1525
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Dielectric Constant 5.2

@Frequency 1e+6 Hz
5.2

@Frequency 1e+6 Hz
ASTM D150
5.7

@Frequency 1000 Hz
5.7

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 24.0 kV/mm

@Thickness 1.60 mm
610 kV/in

@Thickness 0.0630 in
Short Term; ASTM D149
Dissipation Factor 0.012

@Frequency 1000 Hz
0.012

@Frequency 1000 Hz
ASTM D150
0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 145 sec
145 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
UL746A
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F