Shell Carilon® DP P1000 Polyketone  (discontinued **)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® DP P1000 Polyketone  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP P1000 is the first in a family of developmental engineering polyketone resins from Shell Chemical Company. Due to CARILON Polymer's balance of stiffness, toughness, and chemical resistance coupled with its easy processing, CARILON Polymer is expected to find application in the appliance, automotive, electrical, and other industries.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption 0.45 %
0.45 %
24 hour immersion; ASTM D570
Moisture Absorption at Equilibrium 0.53 %
0.53 %
at 50% RH at Equilibrium; ASTM D570
Water Absorption at Saturation 2.1 %
2.1 %
at saturation; ASTM D570
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM D638
Elongation at Break >= 300 %
>= 300 %
ASTM D638
Elongation at Yield 22 %
22 %
ASTM D638
Tensile Modulus 1.60 GPa
232 ksi
ASTM D638
Flexural Strength 55.0 MPa
7980 psi
at 5% strain; ASTM D790
Flexural Modulus 1.60 GPa
232 ksi
ASTM D790
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
0.500 J/cm

@Temperature -40.0 °C
0.937 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Gardner Impact >= 45.0 J
>= 33.2 ft-lb
28.0 J

@Temperature -40.0 °C
20.7 ft-lb

@Temperature -40.0 °F
Tensile Impact Strength 210 kJ/m²
99.9 ft-lb/in²
ASTM D1822
Coefficient of Friction, Dynamic 0.49
0.49
Thrust washer testing against steel at 0.05 m/s (2 in/s) and 2 MPa
Limiting Pressure Velocity 1.10 MPa-m/sec
31400 psi-ft/min
at 0.5 m/s
Taber Abrasion, mg/1000 Cycles 12
12
1 kg load; CS-17 Wheel; ASTM D1044
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ASTM D648
Vicat Softening Point 215 °C
419 °F
ASTM D1525
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Dielectric Constant 5.2

@Frequency 1e+6 Hz
5.2

@Frequency 1e+6 Hz
ASTM D150
5.7

@Frequency 1000 Hz
5.7

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 1.60 mm
533 kV/in

@Thickness 0.0630 in
Short Term; ASTM D149
Dissipation Factor 0.012

@Frequency 1000 Hz
0.012

@Frequency 1000 Hz
ASTM D150
0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 100 sec
100 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
UL746A
Processing Properties Metric English Comments
Melt Temperature 260 °C