Shell Carilon® DB6G6A10 Polyketone, 30% Glass-Reinforced General-Purpose Injection Molding Grade  (discontinue

Category Polymer , Thermoplastic , Polyketone , Polyketone, Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® DB6G6A10 Polyketone, 30% Glass-Reinforced General-Purpose Injection Molding Grade  (discontinue.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6G6A10 is a 30 percent short glass-fiber-reinforced, general purpose injection molding grade, with mechanical properties that classify it as an engineering thermoplastic. This grade shows a unique balance of toughness and high modulus combined with good creep performance, strength and elevated temperature performance. Moreover this polymer exhibits a high resistance to hydrocarbons, solvents, salt solutions, weak acids and weak bases. CARILON Polymer DB6G6A10 is easy to process on standard injection molding equipment. Cycle times are generally short and parts show good mold definition. CARILON Polymers' low moisture sensitivity means that no conditioning of parts before assembly or use is necessary.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Water Absorption 0.42 %
0.42 %
24 hour immersion; ASTM D570
Moisture Absorption at Equilibrium 0.20 %
0.20 %
at 50% RH at Equilibrium; ASTM D570
Water Absorption at Saturation 1.8 %
1.8 %
at saturation; ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore D 83
83
ISO 868
Tensile Strength, Ultimate 130 MPa
18900 psi
ASTM D638
Elongation at Break 3.1 %
3.1 %
ASTM D638
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Flexural Strength 190 MPa
27600 psi
at 5% strain; ASTM D790
Flexural Modulus 7.20 GPa
1040 ksi
ASTM D790
Izod Impact, Notched 1.40 J/cm
2.62 ft-lb/in
0.850 J/cm

@Temperature -40.0 °C
1.59 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Izod Impact, Unnotched 9.10 J/cm
17.0 ft-lb/in
ASTM D256
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 218 °C
424 °F
ASTM D648
Flammability, UL94 HB
HB
Oxygen Index 20 %
20 %
ISO 4589
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Dielectric Constant 5.2

@Frequency 1e+6 Hz
5.2

@Frequency 1e+6 Hz
ASTM D150
6.3

@Frequency 1000 Hz
6.3

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 24.0 kV/mm

@Thickness 1.60 mm
610 kV/in

@Thickness 0.0630 in
Short Term; ASTM D149
Dissipation Factor 0.010

@Frequency 1000 Hz
0.010

@Frequency 1000 Hz
ASTM D150
0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
ASTM D150
Comparative Tracking Index 600 V
600 V
UL746A