Shell Carilon® DB6F5G40 Polyketone, Flame-Retarded (V-0), 20% Glass-Reinforced Injection Molding Grade  (disco

Category Polymer , Thermoplastic , Polyketone , Polyketone, Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® DB6F5G40 Polyketone, Flame-Retarded (V-0), 20% Glass-Reinforced Injection Molding Grade  (disco.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6F5G40 is a flame-retarded, 20 percent glass-fiber-reinforced, injection molding grade with mechanical properties which classify it as an engineering thermoplastic. This high-modulus grade offers a UL94 V-0 rating and high glow-wire index without the use of halogenated or red phosphorus flame retardants. The benign flame-retardant system used for CARILON Polymer DB6F5G40 ensures that the smoke density and toxicity are both low. Yet this grade retains the exceptional blend of properties of the base polymer, such as low moisture absorption, good toughness and high resistance to a wide range of chemicals. CARILON Polymer DB6F5G40 is easy to process on standard injection molding equipment. Cycle times are generally short and parts show good mold definition. CARILON Polymers' low moisture sensitivity means that no conditioning of parts before assembly or use is necessary.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ASTM D792
Water Absorption 0.30 %
0.30 %
24 hour immersion; ASTM D570
Moisture Absorption at Equilibrium 0.45 %
0.45 %
at 50% RH at Equilibrium; ASTM D570
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 110 MPa
16000 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Tensile Modulus 8.00 GPa
1160 ksi
ASTM D638
Flexural Modulus 6.40 GPa
928 ksi
ASTM D790
Izod Impact, Notched 1.12 J/cm
2.10 ft-lb/in
ASTM D256
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 5.5

@Frequency 1e+6 Hz
5.5

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 41.0 kV/mm

@Thickness 0.800 mm
1040 kV/in

@Thickness 0.0315 in
Short Term; ASTM D149
Dissipation Factor 0.030

@Frequency 1e+6 Hz
0.030

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
UL-746A rating 5 (120-180 sec)
Comparative Tracking Index 250 V
250 V
UL746A