Seals Eastern 5723 Fluorocarbon-Elastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Seals Eastern, Inc
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Seals Eastern 5723 Fluorocarbon-Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formulated Viton®. General service.Information provided by Seals Eastern, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.92 g/cc
1.92 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 70
>= 70
ASTM D2240, Type A
80
80
AVG; ASTM D2240, Type A
79

@Temperature 200 °C,
Time 252000 sec
79

@Temperature 392 °F,
Time 70.0 hour
After Dry Heat Aging; ASTM D865
79

@Temperature 200 °C,
Time 1.21e+6 sec
79

@Temperature 392 °F,
Time 336 hour
After Dry Heat Aging; ASTM D865
79

@Temperature 200 °C,
Time 3.60e+6 sec
79

@Temperature 392 °F,
Time 1000 hour
After Dry Heat Aging; ASTM D865
81

@Temperature 200 °C,
Time 605000 sec
81

@Temperature 392 °F,
Time 168 hour
After Dry Heat Aging; ASTM D865
Tensile Strength at Break >= 10.71 MPa
>= 1554 psi
ASTM D412 Method A
16.85 MPa
2444 psi
AVG; ASTM D412 Method A
12.98 MPa

@Temperature 200 °C,
Time 360000 sec
1882 psi

@Temperature 392 °F,
Time 100 hour
After Dry Heat Aging; ASTM D865
14.83 MPa

@Temperature 200 °C,
Time 605000 sec
2151 psi

@Temperature 392 °F,
Time 168 hour
After Dry Heat Aging; ASTM D865
14.83 MPa

@Temperature 200 °C,
Time 1.21e+6 sec
2151 psi

@Temperature 392 °F,
Time 336 hour
After Dry Heat Aging; ASTM D865
15.33 MPa

@Temperature 200 °C,
Time 252000 sec
2224 psi

@Temperature 392 °F,
Time 70.0 hour
After Dry Heat Aging; ASTM D865
Tensile Strength, Yield >= 1.90 MPa
>= 275 psi
Stress at Elongation M50; ASTM D412 Method A
2.30 MPa
333 psi
AVG Stress at Elongation M25; ASTM D412 Method A
>= 3.02 MPa
>= 438 psi
Stress at Elongation M100; ASTM D412 Method A
3.34 MPa
484 psi
AVG Stress at Elongation M50; ASTM D412 Method A
5.78 MPa
839 psi
AVG Stress at Elongation M100; ASTM D412 Method A
Elongation at Break >= 181 %
>= 181 %
ASTM D412 Method A
317 %
317 %
AVG; ASTM D412 Method A
412 %

@Temperature 200 °C,
Time 605000 sec
412 %

@Temperature 392 °F,
Time 168 hour
After Dry Heat Aging; ASTM D865
415 %

@Temperature 200 °C,
Time 1.21e+6 sec
415 %

@Temperature 392 °F,
Time 336 hour
After Dry Heat Aging; ASTM D865
437.5 %

@Temperature 200 °C,
Time 252000 sec
437.5 %

@Temperature 392 °F,
Time 70.0 hour
After Dry Heat Aging; ASTM D865
456.5 %

@Temperature 200 °C,
Time 360000 sec
456.5 %

@Temperature 392 °F,
Time 100 hour
After Dry Heat Aging; ASTM D865
Modulus of Elasticity 0.01590 GPa
2.306 ksi
ASTM D412 Method A
Shear Modulus 0.00530 GPa
0.769 ksi
ASTM D412 Method A
Secant Modulus 0.01495 GPa
2.168 ksi
ASTM D412 Method A
Tear Strength Test 215
215
(psi); ASTM D624, Die B
Compression Set 56 %

@Temperature 200 °C,
Time 79200 sec
56 %

@Temperature 392 °F,
Time 22.0 hour
ASTM D395, Test B
82 %

@Temperature 200 °C,
Time 252000 sec
82 %

@Temperature 392 °F,
Time 70.0 hour
ASTM D395, Test B
91 %

@Temperature 200 °C,
Time 1.21e+6 sec
91 %

@Temperature 392 °F,
Time 336 hour
ASTM D395, Test B
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
400 °F
ASTM D1329
Glass Transition Temp, Tg -20.0 °C
-4.00 °F
ASTM D1329
Processing Properties Metric English Comments
Shelf Life 180 Month
180 Month
ASTM D395, Test B
Descriptive Properties Value Comments
Strain Energy / Unit Volume at 20% Elongation (psi) 41
Users viewing this material also viewed the following: