Seals Eastern 5433 Nitrile Rubber

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Seals Eastern, Inc
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Seals Eastern 5433 Nitrile Rubber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose Nitrile; Low water swellInformation provided by Seals Eastern, Inc.
Mechanical Properties Metric English Comments
Hardness, Shore A >= 65
>= 65
ASTM D2240, Type A
75
75
AVG; ASTM D2240, Type A
73

@Temperature 100 °C,
Time 252000 sec
73

@Temperature 212 °F,
Time 70.0 hour
After Dry Heat Aging; ASTM D865
Tensile Strength at Break >= 16.87 MPa
>= 2447 psi
ASTM D412 Method A
21.64 MPa
3138 psi
AVG; ASTM D412 Method A
22.826 MPa

@Temperature 100 °C,
Time 252000 sec
3310.6 psi

@Temperature 212 °F,
Time 70.0 hour
ASTM D865
Tensile Strength, Yield 0.669 MPa
97.0 psi
AVG Stress at Elongation M25; ASTM D412 Method A
>= 1.59 MPa
>= 231 psi
Stress at Elongation M50; ASTM D412 Method A
2.10 MPa
304 psi
AVG Stress at Elongation M50; ASTM D412 Method A
>= 2.48 MPa
>= 359 psi
Stress at Elongation M100; ASTM D412 Method A
3.96 MPa
575 psi
AVG Stress at Elongation M100; ASTM D412 Method A
Elongation at Break >= 260 %
>= 260 %
ASTM D412 Method A
379 %
379 %
AVG; ASTM D412 Method A
367.6 %

@Temperature 100 °C,
Time 252000 sec
367.6 %

@Temperature 212 °F,
Time 70.0 hour
ASTM D865
Modulus of Elasticity 0.007874 GPa
1.142 ksi
ASTM D412 Method A
Shear Modulus 0.00263 GPa
0.381 ksi
ASTM D412 Method A
Secant Modulus 0.007405 GPa
1.074 ksi
ASTM D412 Method A
Tear Strength Test 324
324
(psi); ASTM D624, Die B
Compression Set 7.5 %

@Temperature 100 °C,
Time 79200 sec
7.5 %

@Temperature 212 °F,
Time 22.0 hour
ASTM D395, Test B
10 %

@Temperature 100 °C,
Time 252000 sec
10 %

@Temperature 212 °F,
Time 70.0 hour
ASTM D395, Test B
Thermal Properties Metric English Comments
Glass Transition Temp, Tg -29.4 °C
-21.0 °F
ASTM D1329
Descriptive Properties Value Comments
Strain Energy / Unit Volume at 20% Elongation (psi) 22