Schwartz Technical Plastics LAMIGAMID® 324 Cast Polyamide 6, MoS2, Heat Stabilized, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized , Nylon 6, MoS2 Filled
Manufacturer Schwartz Technical Plastics
Trade Name LAMIGAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schwartz Technical Plastics LAMIGAMID® 324 Cast Polyamide 6, MoS2, Heat Stabilized, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Application: heavy-duty wheels, running speed up to 3m/sInformation provided by Schwartz Technical Plastics GmbH
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO R 1183
Moisture Absorption at Equilibrium 2.2 %
2.2 %
DIN 53473
Water Absorption at Saturation 7.0 %

@Temperature 20.0 °C
7.0 %

@Temperature 68.0 °F
ISO R 62
Mechanical Properties Metric English Comments
Ball Indentation Hardness 175 MPa
25400 psi
Hc 30; ISO 2039; partially
Tensile Strength, Yield 110 MPa
16000 psi
ISO-DIS 527
Creep Strength >= 12.0 MPa
>= 1740 psi
1% elongation, 1000 h; DIN 53444
>= 18.0 MPa
>= 2610 psi
2% elongation, 1000 h; DIN 53444
Tensile Modulus 3.80 GPa
551 ksi
DIN 53457
Flexural Strength 150 MPa
21800 psi
DIN 54352
Flexural Modulus 3.70 GPa
537 ksi
DIN 53457
Compressive Strength 46.0 MPa
6670 psi
5% pressing; EN ISO 604
66.0 MPa
9570 psi
10% pressing; EN ISO 604
91.0 MPa
13200 psi
20% pressing; EN ISO 604
Izod Impact, Notched (ISO) >= 2.50 kJ/m²
>= 1.19 ft-lb/in²
ISO 180-1A
Izod Impact Resistance NB
NB
swinging hammer 0,1 DIN 51222; DIN 53453
Coefficient of Friction 0.040
0.040
With lubrication
Coefficient of Friction, Dynamic 0.35
0.35
no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C
Tear Strength Test >= 0.15
>= 0.15
ISO-DIS 527
K Factor (Wear Factor) 1.0e-10
1.0e-10
Thermal Properties Metric English Comments
CTE, linear 70.0 - 80.0 µm/m-°C

@Temperature 20.0 - 100 °C
38.9 - 44.4 µin/in-°F

@Temperature 68.0 - 212 °F
DIN 53752
Specific Heat Capacity 1.67 J/g-°C
0.399 BTU/lb-°F
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
ISO R 1218
Maximum Service Temperature, Air 120 °C
248 °F
Continuous
180 °C
356 °F
Intermittent
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
V-notch; ISO R 75
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
V-notch; ISO R 75
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Continuous
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
DIN 53482
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
DIN 53482
Dielectric Constant 3.7
3.7
DIN 53483
Dielectric Strength 50.0 kV/mm
1270 kV/in
DIN 53481
Dielectric Loss Index 0.030
0.030
DIN 53483
Descriptive Properties Value Comments
Creepage/leakage Resistance KA3c
DIN 53480