Schott Glass 8516 Sealing Glass
| Category | Ceramic , Glass |
| Manufacturer | Schott North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schott Glass 8516 Sealing Glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Sealing glass for Fe-Ni alloys, high IR-absorbing, lead-free, of poor evaporation Reed switches The heavy metal content for the elements lead, cadmium, mercury, and hexavalent chromium is below 100 ppmInformation provided by SCHOTT AG.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.56 g/cc @Temperature 25.0 °C |
0.0925 lb/in³ @Temperature 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 72.0 GPa | 10400 ksi | |
| Poissons Ratio | 0.21 | 0.21 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.90 µm/m-°C @Temperature 20.0 - 300 °C |
4.94 µin/in-°F @Temperature 68.0 - 572 °F |
ISO 7991 |
| Thermal Conductivity | 1.10 W/m-K @Temperature 90.0 °C |
7.63 BTU-in/hr-ft²-°F @Temperature 194 °F |
|
| Transformation Temperature, Tg | 447 °C | 837 °F | ISO 7884-8 |
| Softening Point | 646 °C | 1190 °F | Viscosity 10<sup>7.6</sup> dPa s; ISO 7884-3 |
| Working Point | 990 °C | 1810 °F | Viscosity 10<sup>4</sup> dPa s; ISO 7884-2 |
| Annealing Point | 445 °C | 833 °F | Viscosity 10<sup>13</sup> dPa s; ISO 7884-4 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.516 @Wavelength 587.6 nm |
1.516 @Wavelength 587.6 nm |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.50e+6 ohm-cm @Temperature 350 °C |
2.50e+6 ohm-cm @Temperature 662 °F |
|
| 1.30e+8 ohm-cm @Temperature 250 °C |
1.30e+8 ohm-cm @Temperature 482 °F |
||
| Dielectric Constant | 6.5 @Frequency 1.00e+6 Hz, Temperature 25.0 °C |
6.5 @Frequency 1.00e+6 Hz, Temperature 77.0 °F |
|
| Dielectric Loss Index | 0.0025 @Frequency 1.00e+6 Hz, Temperature 25.0 °C |
0.0025 @Frequency 1.00e+6 Hz, Temperature 77.0 °F |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Acid Class, SR | 1 | 1 | DIN 12116 |
| Alkali Class, AR | 2 | 2 | ISO 695 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hydrolytic Resistance | Class HGB 3 | ISO 719 |
| Stress-optical Coefficient K (10-6mm2N-1) | 3 | DIN 52314 |
| tk100(°C) | 250 |
Users viewing this material also viewed the following:
- Chevron Phillips 7120ST LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- Plenco 304 Black Impact Grade Woodflour/Cellulose Filled Phenolic Molding Compound (discontinued **)
- Momentive Performance Materials HPC Boron Nitride (BN)/TiO2 Water Based Coating
- Saint-Gobain CHR® SG36-05(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Tipco Tipcolite® TMS 311 Phenolic Compound, Cotton, Filler & Wood Flour, having Medium Flow & High Strength
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- Bulk Molding Compounds BMC 5436 Mineral Filled, Glass Reinforced Polyester
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Atomite Whiting Filler
- Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved