Schmolz + Bickenbach UGIMA® 304 Cu Stainless Steel Bar

Category Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name UGIMA®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach UGIMA® 304 Cu Stainless Steel Bar.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 304Cu UGIMA® is an enhanced machining grade produced only by Ugitech, providing the ultimate level of machinability available in an non-resulfurized austenitic stainless steel. 304Cu UGIMA® also features the added benefit of increased cold formability when compared with that of standard type 304 stainless steels. The increased copper content in 304Cu UGIMA® provides corrosion resistance superior to 304L and comparable to 316L. The unique combination of machinability, cold formability, and corrosion resistance afforded by 304Cu UGIMA® is unique in the industry, and provides the optimum solution for even the most difficult fabrication challenges. 304Cu UGIMA® builds upon the proprietary UGIMA manufacturing process with the addition of copper, allowing for good machinability across a wide range of operations and cutting conditions. It allows for superior machinabilty at both low and high speeds, cam-driven and CNC machines, and with high-speed steel or carbide tooling. Machine shops using 304Cu UGIMA® have experienced consistent success regardless of machine, operation, tooling, or cutting conditions. From lot to lot 304Cu UGIMA® is engineered to give the same high performance every time without surprises.Information provided by Schmolz + Bickenbach
Physical Properties Metric English Comments
Density 7.81 g/cc
0.282 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 145 - 185

@Thickness >=25.4 mm
145 - 185

@Thickness >=1.00 in
Turned Bars
180 - 210

@Thickness <=25.4 mm
180 - 210

@Thickness <=1.00 in
Cold Drawn Bars
Tensile Strength 483 - 621 MPa

@Thickness >=25.4 mm
70000 - 90000 psi

@Thickness >=1.00 in
Turned Bars
586 - 724 MPa

@Thickness <=25.4 mm
85000 - 105000 psi

@Thickness <=1.00 in
Cold Drawn Bars
Tensile Strength, Yield 207 - 345 MPa

@Strain 0.200 %,
Thickness >=25.4 mm
30000 - 50000 psi

@Strain 0.200 %,
Thickness >=1.00 in
Turned Bars
483 - 621 MPa

@Strain 0.200 %,
Thickness <=25.4 mm
70000 - 90000 psi

@Strain 0.200 %,
Thickness <=1.00 in
Cold Drawn Bars
Elongation at Yield 28 - 40 %

@Thickness <=25.4 mm
28 - 40 %

@Thickness <=1.00 in
Cold Drawn Bars
48 - 62 %

@Thickness >=25.4 mm
48 - 62 %

@Thickness >=1.00 in
Turned Bars
Reduction of Area 68 - 75 %

@Thickness <=25.4 mm
68 - 75 %

@Thickness <=1.00 in
Cold Drawn Bars
70 - 82 %

@Thickness >=25.4 mm
70 - 82 %

@Thickness >=1.00 in
Turned Bars
Modulus of Elasticity 200 GPa

@Temperature 20.0 °C
29000 ksi

@Temperature 68.0 °F
Tension
200 GPa

@Temperature 500 °C
29000 ksi

@Temperature 932 °F
Tension
Thermal Properties Metric English Comments
CTE, linear 1.80 µm/m-°C

@Temperature 20.0 - 500 °C
1.00 µin/in-°F

@Temperature 68.0 - 932 °F
16.5 µm/m-°C

@Temperature 20.0 - 200 °C
9.17 µin/in-°F

@Temperature 68.0 - 392 °F
Thermal Conductivity 16.7 W/m-K

@Temperature 20.0 °C
116 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
18.0 W/m-K

@Temperature 500 °C
125 BTU-in/hr-ft²-°F

@Temperature 932 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.10 %
<= 0.10 %
Chromium, Cr 17 - 19 %
17 - 19 %
Copper, Cu 3.0 - 4.0 %
3.0 - 4.0 %
Iron, Fe >= 63.825 %
>= 63.825 %
Manganese, Mn <= 2.0 %
<= 2.0 %
Nickel, Ni 8.0 - 10 %
8.0 - 10 %
Phosphorous, P <= 0.045 %
<= 0.045 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S <= 0.030 %
<= 0.030 %
Processing Properties Metric English Comments
Hot-Working Temperature >= 954 °C
>= 1750 °F
Forge
999 - 1200 °C
1830 - 2190 °F
Forging range
1150 - 1220 °C
2100 - 2230 °F
Heat in range
<= 1290 °C
<= 2350 °F
Heat of core during fast forging
Descriptive Properties Value Comments
Corrosion Resistance Acetic Acid
2/4
Humidity
4/4
NaCl (Saline Mist)
3/4
Nitric Acid
2/4
Petroleum
2/4
Phosphoric Acid
3/4
Sodium Carbonate
2/4
Sulfuric Acid
3/4