Schmolz + Bickenbach Formadur® PH X Superclean Plastic Mold Steel
| Category | Metal , Ferrous Metal , Martensitic , Tool Steel , Mold Steel |
| Manufacturer | Schmolz + Bickenbach (Swiss Steel International) |
| Trade Name | Formadur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schmolz + Bickenbach Formadur® PH X Superclean Plastic Mold Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Formadur® PH X Superclean is a corrosion-resistant, martensitic precipitation hardened stainless steelCharacteristics: Excellent resistance to corrosion; Excellent polishability; Excellent dimensional stability; Good strength; and Good toughnessApplications: Formadur® PH X Superclean is recommended for tools/molds for the processing of corrosive plastics.Information provided by Schmolz + Bickenbach
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.89 g/cc | 0.285 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 34 @Treatment Temp. 593 °C, Time 14400 sec |
34 @Treatment Temp. 1100 °F, Time 4.00 hour |
|
| 38 @Treatment Temp. 551.7 °C, Time 14400 sec |
38 @Treatment Temp. 1025 °F, Time 4.00 hour |
||
| 41 @Treatment Temp. 496 °C, Time 14400 sec |
41 @Treatment Temp. 925 °F, Time 4.00 hour |
||
| 42 @Treatment Temp. 399 °C, Time 14400 sec |
42 @Treatment Temp. 750 °F, Time 4.00 hour |
||
| 43 @Treatment Temp. 454 °C, Time 14400 sec |
43 @Treatment Temp. 850 °F, Time 4.00 hour |
||
| 44 @Treatment Temp. 482 °C, Time 14400 sec |
44 @Treatment Temp. 900 °F, Time 4.00 hour |
||
| Tensile Strength | 1120 MPa | 162000 psi | 38 HRC |
| 1190 MPa | 172000 psi | 40 HRC | |
| 1240 MPa | 180000 psi | 42 HRC | |
| Tensile Strength, Yield | 1100 MPa @Strain 0.200 % |
160000 psi @Strain 0.200 % |
38 HRC |
| 1170 MPa @Strain 0.200 % |
170000 psi @Strain 0.200 % |
40 HRC | |
| 1210 MPa @Strain 0.200 % |
175000 psi @Strain 0.200 % |
42 HRC | |
| Elongation at Yield | 12.2 % | 12.2 % | 40 HRC |
| 12.2 % | 12.2 % | 42 HRC | |
| 12.8 % | 12.8 % | 38 HRC | |
| Charpy Impact | 33.9 J | 25.0 ft-lb | Notched; at 38 HRC |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.6 µm/m-°C @Temperature 21.1 - 93.3 °C |
5.90 µin/in-°F @Temperature 70.0 - 200 °F |
|
| 10.8 µm/m-°C @Temperature 21.1 - 204 °C |
6.00 µin/in-°F @Temperature 70.0 - 400 °F |
||
| 16.6 µm/m-°C @Temperature 21.1 - 399 °C |
9.20 µin/in-°F @Temperature 70.0 - 750 °F |
||
| Thermal Conductivity | 16.6 W/m-K @Temperature 21.1 °C |
115 BTU-in/hr-ft²-°F @Temperature 70.0 °F |
|
| 18.0 W/m-K @Temperature 149 °C |
125 BTU-in/hr-ft²-°F @Temperature 300 °F |
||
| 22.3 W/m-K @Temperature 504 °C |
155 BTU-in/hr-ft²-°F @Temperature 940 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.050 % | 0.050 % | |
| Chromium, Cr | 15 % | 15 % | |
| Copper, Cu | 3.5 % | 3.5 % | |
| Iron, Fe | 76.95 % | 76.95 % | |
| Nickel, Ni | 4.5 % | 4.5 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Corrosion Properties/Weight loss rate | 0.2% Hydrochloric Acid | 0.0017 g/hm<sup>2</sup> |
| 5% Acetic Acid | 0.018 g/hm<sup>2</sup> | |
| 5% Nitric Acid | 0.0015 g/hm<sup>2</sup> | |
| 5% Sulphuric Acid | 5 g/hm<sup>2</sup> |