Schmolz + Bickenbach Formadur® 2311 Plastic Mold Steel
| Category | Metal , Ferrous Metal , Tool Steel , Mold Steel |
| Manufacturer | Schmolz + Bickenbach (Swiss Steel International) |
| Trade Name | Formadur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schmolz + Bickenbach Formadur® 2311 Plastic Mold Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Formadur® 2311 is a pre-hardened plastic mold steelCharacteristics: Good texturing compared to Formadur®2312 and Good polishability compared to Formadur® 231Applications: Injection molds, Compression molds, Blow mold, Mold bases and Die holderInformation provided by Schmolz + Bickenbach
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.83 g/cc | 0.283 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 28 @Treatment Temp. 700.0 °C, Time 7200 sec |
28 @Treatment Temp. 1292 °F, Time 2.00 hour |
|
| 36 @Treatment Temp. 600.0 °C, Time 7200 sec |
36 @Treatment Temp. 1112 °F, Time 2.00 hour |
||
| 42 @Treatment Temp. 500 °C, Time 7200 sec |
42 @Treatment Temp. 932 °F, Time 2.00 hour |
||
| 46 @Treatment Temp. 400 °C, Time 7200 sec |
46 @Treatment Temp. 752 °F, Time 2.00 hour |
||
| 48 @Treatment Temp. 300 °C, Time 7200 sec |
48 @Treatment Temp. 572 °F, Time 2.00 hour |
||
| 50 @Treatment Temp. 200 °C, Time 7200 sec |
50 @Treatment Temp. 392 °F, Time 2.00 hour |
||
| 51 @Treatment Temp. 100 °C, Time 7200 sec |
51 @Treatment Temp. 212 °F, Time 2.00 hour |
||
| Tensile Strength | 924 MPa | 134000 psi | 32 HRC |
| 848 MPa @Treatment Temp. 700.0 °C |
123000 psi @Treatment Temp. 1292 °F |
28 HRC | |
| 1140 MPa @Treatment Temp. 600.0 °C |
165000 psi @Treatment Temp. 1112 °F |
36 HRC | |
| 1330 MPa @Treatment Temp. 500 °C |
193000 psi @Treatment Temp. 932 °F |
42 HRC | |
| 1480 MPa @Treatment Temp. 400 °C |
215000 psi @Treatment Temp. 752 °F |
46 HRC | |
| 1570 MPa @Treatment Temp. 300 °C |
228000 psi @Treatment Temp. 572 °F |
48 HRC | |
| 1670 MPa @Treatment Temp. 200 °C |
242000 psi @Treatment Temp. 392 °F |
50 HRC | |
| 1730 MPa @Treatment Temp. 100 °C |
251000 psi @Treatment Temp. 212 °F |
51 HRC |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.2 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.80 µin/in-°F @Temperature 70.0 - 200 °F |
|
| 13.0 µm/m-°C @Temperature 21.1 - 204 °C |
7.20 µin/in-°F @Temperature 70.0 - 400 °F |
||
| 13.3 µm/m-°C @Temperature 21.1 - 302 °C |
7.40 µin/in-°F @Temperature 70.0 - 575 °F |
||
| Thermal Conductivity | 31.8 W/m-K @Temperature 302 °C |
221 BTU-in/hr-ft²-°F @Temperature 575 °F |
|
| 33.6 W/m-K @Temperature 204 °C |
233 BTU-in/hr-ft²-°F @Temperature 400 °F |
||
| 33.9 W/m-K @Temperature 100 °C |
235 BTU-in/hr-ft²-°F @Temperature 212 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.40 % | 0.40 % | |
| Chromium, Cr | 1.9 % | 1.9 % | |
| Iron, Fe | 96 % | 96 % | |
| Manganese, Mn | 1.5 % | 1.5 % | |
| Molybdenum, Mo | 0.20 % | 0.20 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Annealing Temperature | 710 - 740.6 °C | 1310 - 1365 °F | Cooling: Furnace; < 235 HB |