Schmolz + Bickenbach Formadur® 2085 Plastic Mold Steel

Category	Metal , Ferrous Metal , Tool Steel , Mold Steel
Manufacturer	Schmolz + Bickenbach (Swiss Steel International)
Trade Name	Formadur®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Schmolz + Bickenbach Formadur® 2085 Plastic Mold Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: FORMADUR 2085 is a free-machining corrosion-resistant mold frame steelCharacteristics: Lower mold production costs due to improved machinability; Improved corrosion resistance compared to Corroplast and Uniform hardnessApplications: Mold frames for processing corrosive plastics, Mold components and Plastic extrusion componentsHeat Treatment: 1560°F- 1610°F; Cooling: Furnace 20°F/hour to 1200°F, Then air cools; Hardness:

Physical Properties	Metric	English	Comments
Density	7.75 g/cc	0.280 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	28 @Treatment Temp. 200 °C	28 @Treatment Temp. 392 °F
	30 @Treatment Temp. 600.0 °C	30 @Treatment Temp. 1112 °F
	36 @Treatment Temp. 550.0 °C	36 @Treatment Temp. 1022 °F
	46 @Treatment Temp. 400 °C	46 @Treatment Temp. 752 °F
	47 @Treatment Temp. 300 °C	47 @Treatment Temp. 572 °F
	47 @Treatment Temp. 450 °C	47 @Treatment Temp. 842 °F
	47 @Treatment Temp. 500 °C	47 @Treatment Temp. 932 °F
	48 @Treatment Temp. 100 °C	48 @Treatment Temp. 212 °F
Tensile Strength	1100 MPa @Temperature -5.56 °C	160000 psi @Temperature 22.0 °F	Hardened and tempered to 34 HRC
Tensile Strength, Yield	965 MPa @Temperature 22.0 °C	140000 psi @Temperature 71.6 °F	Hardened and tempered to 34 HRC
Elongation at Yield	12 % @Temperature 22.0 °C	12 % @Temperature 71.6 °F	Hardened and tempered to 34 HRC
Reduction of Area	45 % @Temperature 22.0 °C	45 % @Temperature 71.6 °F	Hardened and tempered to 34 HRC

Thermal Properties	Metric	English	Comments
CTE, linear	11.5 µm/m-°C @Temperature 21.1 - 204 °C	6.40 µin/in-°F @Temperature 70.0 - 400 °F
Thermal Conductivity	23.5 W/m-K @Temperature 93.3 °C	163 BTU-in/hr-ft²-°F @Temperature 200 °F

Component Elements Properties	Metric	English
Carbon, C	0.33 %	0.33 %
Chromium, Cr	16 %	16 %
Iron, Fe	83.12 %	83.12 %
Nickel, Ni	0.50 %	0.50 %
Sulfur, S	0.050 %	0.050 %

Processing Properties	Metric	English	Comments
Annealing Temperature	999 - 1050 °C	1830 - 1920 °F	Soft; Hold at temperature for 30 min; Cooling: Oil; Quenched < 48 HRC