Sax Polymers SAXLAC 835U Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Sax Polymers |
| Trade Name | SAXLAC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXLAC 835U Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Saxalac 835U is an antistatic, easy flowing light stabilized ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Mechanical property data tested at 50% RH.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 35 g/10 min @Load 10.0 kg, Temperature 220 °C |
35 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 40.0 MPa | 5800 psi | ISO 527-1 |
| Elongation at Break | 10 % | 10 % | ISO 527-1 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 22.0 kJ/m² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 90.0 °C @Thickness 2.00 mm |
194 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 95.0 °C | 203 °F | 50B; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|
| Glow Wire Test | 650 °C | 1200 °F | IE/CEN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Dry Blend E0101 Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics Valox® FXV310SK PBT (Europe-Africa-Middle East)
- American Polymers 370 Polystyrene, High Heat
- Diamond Polymers ABS 7600B (ELG)
- Eurotec® Tecomid® NA40 KK30 NL PA 6.6 30% glass fiber/mineral reinforced, low warpage
- EMS-Grivory Grivory® XE 4217 black 9233 PA6T/66-GF45
- Epoxy Technology EPO-TEK® H20E-175 Electrically Conductive, Silver Epoxy
- Kazanorgsintez PE2NT 11-285D High Density Polyethylene Composite
- DuPont Performance Polymers VTR 8605 (GF-S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued **
Copyright © lookpolymers.com All Rights Reserved