Sawbones Solid Rigid Polyurethane Foam 5 pcf Density

Category Other Engineering Material , Composite Core Material , Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane Foam, Unreinforced
Manufacturer Sawbones
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sawbones Solid Rigid Polyurethane Foam 5 pcf Density.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Solid Rigid Polyurethane FoamPrimary UseSolid rigid polyurethane foam is primarily used as an alternative test medium for human cancellous bone. These products are not intended to replicate the mechanical properties of human bone, however, it does provide consistent and uniform material with properties in the range of human cancellous bone. Relevant mechanical properties for comparison to human cancellous bone may depend on the particular test method that is being developed.The ASTM F-1839-08 "Standard Specification for Rigid Polyurethane Foam for Use as a Standard Material for Testing Orthopaedic Devices and Instruments" states that, "The uniformity and consistent properties of rigid polyurethane foam make it an ideal material for comparative testing of bones screws and other medical devices and instruments."DescriptionSolid rigid polyurethane foam has a closed cell content ranging from 96.0 to 99.9%. Foam is available in a range of sizes and densities, from 0.08 to 0.80 grams per cubic centimeter (5 to 50 pounds per cubic foot).. Standard block size: 13cm X 18cm X 4cm Standard sheet size: 13cm X 18cm X 3mm Other NotesWater absorption ranges from 0.301 to 0.0 kg/m2Foam meets ASTM F-1839-08. Block dimensions are within ±2mm and sheet thickness is within ±0.3mm. Foam density may vary ±10%. Properties parallel to direction of the rise of foam. Information provided by Sawbones.
Physical Properties Metric English Comments
Density 0.0800 g/cc
0.00289 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength 1.00 MPa
145 psi
Tensile Modulus 0.0320 GPa
4.64 ksi
Compressive Yield Strength 0.600 MPa
87.0 psi
Compressive Modulus 0.0160 GPa
2.32 ksi
Poissons Ratio 0.30
0.30
Calculated
Shear Modulus 0.00710 GPa
1.03 ksi
Shear Strength 0.590 MPa
85.6 psi
Thermal Properties Metric English Comments
CTE, linear 63.0 µm/m-°C

@Temperature -46.0 - 93.0 °C
35.0 µin/in-°F

@Temperature -50.8 - 199 °F