Samyang Triloy® 410 PC/PET alloy  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samyang Triloy® 410 PC/PET alloy  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Impact resistantHeat resistantDimensional stabilityProcessabilityGood flowApplications:O/A partRear view mirror housingRice cooker baseAll information provided by Samyang
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Water Absorption 0.15 %

@Time 86400 sec
0.15 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0070 - 0.012 cm/cm

@Thickness 3.00 mm
0.0070 - 0.012 in/in

@Thickness 0.118 in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 250 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength, Yield 53.9 MPa
7820 psi
ASTM D638
Elongation at Break 120 %
120 %
ASTM D638
Flexural Yield Strength 78.5 MPa
11400 psi
ASTM D790
Flexural Modulus 1.96 GPa
284 ksi
ASTM D790
Izod Impact, Unnotched 7.85 J/cm

@Thickness 3.17 mm
14.7 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 83.0 µm/m-°C
46.1 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm
584 kV/in
ASTM D149
Dissipation Factor 0.0090

@Frequency 1.00e+6 Hz
0.0090

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 121 sec
121 sec
ASTM D495
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 250 °C
446 - 482 °F
Middle Barrel Temperature 220 - 240 °C
428 - 464 °F
Front Barrel Temperature 210 - 230 °C
410 - 446 °F
Nozzle Temperature 240 - 250 °C
464 - 482 °F
Melt Temperature 240 - 250 °C
464 - 482 °F
Drying Temperature 120 °C
248 °F
Dry Time 3 - 5 hour
3 - 5 hour
Moisture Content <= 0.020 %
<= 0.020 %
Screw Speed 30 - 80 rpm
30 - 80 rpm