Samsung Cheil Industries Starex® TX-0520T TRABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® TX-0520T TRABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 43.1 MPa | 6260 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 58.8 MPa | 8530 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 3.17 mm |
2.76 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 87.0 °C | 189 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
ASTM D1003 |
| Transmission, Visible | 88 % @Thickness 3.20 mm |
88 % @Thickness 0.126 in |
ASTM D1003 |
Users viewing this material also viewed the following:
- Outokumpu 4432 Cr-Ni-Mo Austenitic Stainless Steel
- SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS
- Osprey Metals 17-4 PH/MA Stainless Steel Master Alloy Powder (Grade 90% - 22)
- Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes
- Master Bond EP30HT-LO NASA Low Outgassing, Optically Clear Coating
- Westlake Plastics Pomalux® Acetal Copolymer, Compression Molded
- DuPont™ Nomex® 414 Paper, 10 mil Nominal Thickness
- Arlon 41300R062 0.062" Uncured Silicone Rubber on Holland Cloth
- DuPont Performance Polymers Neoprene GNA M1 Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved