Samsung Cheil Industries Starex® LX-0971 S ABS, Unreinforced Metallic-Look

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® LX-0971 S ABS, Unreinforced Metallic-Look.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Melt Flow 16 g/10 min

@Load 10.0 kg,
Temperature 220 °C
16 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength at Break 33.3 MPa
4830 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ASTM D638
Elongation at Break 16 %
16 %
50 mm/min; ASTM D638
Tensile Modulus 2.16 GPa
313 ksi
50 mm/min; ASTM D638
Flexural Strength 69.6 MPa
10100 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.35 GPa
341 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.96 J/cm

@Thickness 6.35 mm
3.67 ft-lb/in

@Thickness 0.250 in
ASTM D256
2.06 J/cm

@Thickness 3.17 mm
3.86 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 6.40 mm
203 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 6.40 mm
208 °F

@Thickness 0.252 in
ASTM D648
Vicat Softening Point 88.0 °C
190 °F
B/50; ISO R306
100 °C
212 °F
B/120; ISO R306