Samsung Cheil Industries Starex® LX-0970 LS ABS, Unreinforced Metallic-Look

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® LX-0970 LS ABS, Unreinforced Metallic-Look.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength at Break 33.3 MPa
4830 psi
5 mm/min; ASTM D638
Tensile Strength, Yield 43.1 MPa
6260 psi
50 mm/min; ASTM D638
Elongation at Break 9.3 %
9.3 %
5 mm/min; ASTM D638
Tensile Modulus 2.16 GPa
313 ksi
5 mm/min; ASTM D638
Flexural Strength 68.6 MPa
9950 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.26 GPa
327 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.57 J/cm

@Thickness 6.35 mm
2.94 ft-lb/in

@Thickness 0.250 in
ASTM D256
1.67 J/cm

@Thickness 3.17 mm
3.12 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C

@Thickness 6.40 mm
201 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C

@Thickness 6.40 mm
192 °F

@Thickness 0.252 in
ASTM D648
Vicat Softening Point 98.0 °C
208 °F
B/50; ISO R306
99.0 °C
210 °F
B/120; ISO R306