Samsung Cheil Industries Starex® LX-0951 ABS, Unreinforced Metallic-Look

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® LX-0951 ABS, Unreinforced Metallic-Look.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Water Absorption 0.050 %

@Temperature 23.0 °C
0.050 %

@Temperature 73.4 °F
ASTM D570
Melt Flow 29 g/10 min

@Load 10.0 kg,
Temperature 220 °C
29 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 45.1 MPa
6540 psi
50 mm/min; ASTM D638
Elongation at Break 14 %
14 %
50 mm/min; ASTM D638
Flexural Strength 67.7 MPa
9820 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.35 GPa
341 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.37 J/cm

@Thickness 6.35 mm
2.57 ft-lb/in

@Thickness 0.250 in
ASTM D256
1.47 J/cm

@Thickness 3.17 mm
2.76 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 6.40 mm
185 °F

@Thickness 0.252 in
ASTM D648
Vicat Softening Point 96.0 °C
205 °F
B/50; ISO R306